5917T SEAFLO NEO CF PREMIUM Tin-free Copper-free Self-polishing Antifouling Paint belongs to Antifouling. It is a copper-free high-performance hydrolysing antifouling paint based on zinc acrylate polymer and containing special synthetic agents developed from pharmacology. This antifouling paint can be applied to vessels engaged in trade at various speeds and frequencies of navigation, with main emphasis on maintaining good hull appearance over the long term, reducing hull resistance and saving fuel. Parameters on this page: Volume Solids 45 ± 2% (by volume), Dry Film Thickness (DFT) 75–160 µm, Theoretical Spreading Rate 0.167–0.356 L/m².
Parameter source: CMP original technical data sheet (TDS) “5917T SEAFLO NEO CF PREMIUM Tin-free Copper-free Self-polishing Antifouling Paint”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 45 ± 2% (by volume) |
|---|---|
| Dry Film Thickness | 75–160 µm |
| Theoretical Spreading Rate | 0.167-0.356 L/m2 |
| VOC | 465 g/L |
| Density / Specific Gravity | 1.49g/ml |
| Number of Components | One-component |
| Flash Point | 24.5°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red, light red |
It is a copper-free high-performance hydrolysing antifouling paint based on zinc acrylate polymer and containing special synthetic agents developed from pharmacology. This antifouling paint can be applied to vessels engaged in trade at various speeds and frequencies of navigation, with main emphasis on maintaining good hull appearance over the long term, reducing hull resistance and saving fuel.
| Type | Tin-free, copper-free self-polishing antifouling |
|---|---|
| Use | Can be used as an antifouling paint for ocean-going steel-hulled vessels to extend dry-docking intervals |
| Colour | Red, light red |
|---|---|
| Flash Point | 24.5°C |
| Density | 1.49g/ml |
| Volume Solids | 45 ± 2% (by volume) |
| Volatile organic compound content | 465 g/L |
| Theoretical spreading rate | 0.167-0.356 L/m2 |
| Thickness | WFT 167–356 µm, DFT 75–160 µm |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 6 h | 4 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 48 h | 36 h | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | SILVAX SQ-K, BANNOH 1500 N, BANNOH 1500 N Z, BANNOH 1500 S, BANNOH 1500 S Z, BANNOH 500 R, BANNOH 500 S and other products |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6. Slight colour change may occur after immersion and outdoor exposure.
7 Density, solids content and volatile organic compounds are calculated values without thinner addition. The values vary with colour, production process, local regulations and other factors.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.