5913A SEAFLO NEO-S Tin-free Self-polishing Antifouling Paint is an antifouling paint. SEAFLO NEO-S is a tin-free self-polishing antifouling paint based on a highly hydrolysing silyl polymer. Parameters on this page: volume solids 48 ± 2% (by volume), dry film thickness 40–150 µm, theoretical spreading rate 0.083–0.312 L/m². Comparable products of the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling Paint, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling Paint, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling Paint.
Data source: CMP original Technical Data Sheet (TDS), "5913A SEAFLO NEO-S Tin-free Self-polishing Antifouling Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 48 ± 2% (by volume) |
|---|---|
| Dry Film Thickness | 40–150 µm |
| Theoretical Spreading Rate | 0.083-0.312 L/m2 |
| VOC | 476 g/L (Method 24) |
| Density / Specific Gravity | 1.67g/ml |
| Number of Components | One-component |
| Flash Point | 26.1°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red, light red |
SEAFLO NEO-S is a tin-free self-polishing antifouling based on a silane polymer with high hydrolysis activity.
Provides high static antifouling performance and low friction.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | May be used as additional antifouling during newbuilding outfitting. |
| Colour | Red, light red |
|---|---|
| Flash Point | 26.1°C |
| Density | 1.67g/ml (ISO 2811) |
| Volume Solids | 48 ± 2% (by volume) (ISO 3233) |
| Volatile organic compound content | 476 g/L (Method 24) |
| Theoretical spreading rate | 0.083-0.312 L/m2 |
| Thickness | Wet film 83–313 µm; dry film 40–150 µm |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 6 h | 4 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 48 h | 36 h | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5 - 2.5 Pa.s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | SEAFLO NEO, SEAFLO NEO SL, etc. |
Subsequent coat:
| Packaging | One-component |
|---|
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6. Slight colour change may occur after immersion and outdoor exposure.
7. Density, solids content and VOC content are theoretical calculated values without added thinner. Values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.