5911 SEA GRANDPRIX 2000 Tin-Free Self-Polishing Antifouling is an antifouling. Good antifouling performance comes from the highly active polymer, which ensures greater efficacy and release of the biocide. Parameters on this page: volume solids 44 ± 2% (by volume), dry film thickness 40-150 µm, theoretical spreading rate 0.091-0.341 L/m². Comparable models from the same brand: 4010B SEATENDER 7 Tin-Free Self-Polishing Antifouling, 5843A SEAFLO NEO SL Tin-Free Self-Polishing Antifouling, 5843H SEAFLO NEO SL Z Tin-Free Self-Polishing Antifouling.
Parameter source: CMP original technical data sheet (TDS) for 5911 SEA GRANDPRIX 2000 Tin-Free Self-Polishing Antifouling; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 44 ± 2% (by volume) |
|---|---|
| Dry Film Thickness | 40–150 µm |
| Theoretical Spreading Rate | 0.091-0.341 L/m2 |
| VOC | 497 g/L |
| Density / Specific Gravity | 1.68g/ml |
| Number of Components | One-component |
| Flash Point | 23.2°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red, light red, blue, purple, black |
SEA GRANDPRIX 2000 is a tin-free self-polishing antifouling based on a special resin with high hydrolysis activity.
Good antifouling performance derives from the highly active polymer, which ensures high efficacy and release of the biocide.
Provides long-term antifouling protection through a controlled hydrolysis maintaining surface activity.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | May be used as an antifouling for the bottoms of offshore steel vessels. |
| Colour | Red, light red, blue, purple, black |
|---|---|
| Flash Point | 23.2°C |
| Density | 1.68g/ml |
| Volume Solids | 44 ± 2% (by volume) (ISO 3233) |
| Volatile organic compound content | 497 g/L |
| Theoretical spreading rate | 0.091-0.341 L/m2 |
| Thickness | Wet film 91-341 µm; dry film 40-150 µm |
(dry film 125 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 6 h | 4 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 48 h | 36 h | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5 - 2.5 Pa.s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0-5% by volume. SILVAX SQ-K, CMP AC-10, RAVAX AC-HB, BANNOH 500 R, BANNOH previous coats |
500 N, BANNOH 500 S, BANNOH 1500 N, BANNOH 1500 S, etc.
Subsequent coat:
| Packaging | One-component |
|---|
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6. Slight colour change may occur after immersion and outdoor exposure.
7. Density, solids content and VOC content are theoretical values based on a typical colour (red) formulation without thinner.
Values vary according to colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.