5908A SEA GRANDPRIX MARK II Tin-free Self-Polishing Antifouling Paint belongs to antifouling paints. Good antifouling performance derives from the highly active polymer, which ensures greater efficacy and release of the biocide. Parameters on this page: Volume Solids 55 ± 2% (by volume) (ISO:3233), Dry Film Thickness 75–160 µm, Theoretical Spreading Rate 0.136–0.291 L/m². Comparable models from the same brand: 4010B SEATENDER 7 Tin-free Self-Polishing Antifouling Paint, 5843A SEAFLO NEO SL Tin-free Self-Polishing Antifouling Paint, 5843H SEAFLO NEO SL Z Tin-free Self-Polishing Antifouling Paint.
Parameter source: CMP original Technical Data Sheet (TDS) “5908A SEA GRANDPRIX MARK II Tin-free Self-Polishing Antifouling Paint”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 55 ± 2% (by volume) (ISO 3233) |
|---|---|
| Dry Film Thickness | 75–160 µm |
| Theoretical Spreading Rate | 0.136-0.291 L/m2 |
| VOC | 425 g/L (Method24) |
| Density / Specific Gravity | 1.76g/ml (ISO:2811) |
| Number of Components | One-component |
| Flash Point | 29.3°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Brown, light brown |
SEA GRANDPRIX MARK II is a high-performance hydrolysing antifouling paint based on silyl polymer. Good antifouling performance derives from the highly active polymer, which ensures greater efficacy and release of the biocide. The surface activation energy maintained through controlled hydrolysis provides long-term antifouling protection.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | Suitable as a bottom antifouling for ocean-going steel ships to extend docking intervals. |
| Colour | Brown, light brown |
|---|---|
| Flash Point | 29.3°C |
| Density | 1.76g/ml (ISO:2811) |
| Volume Solids | 55 ± 2% (by volume) (ISO 3233) |
| Volatile organic compound content | 425 g/L (Method24) |
| Theoretical spreading rate | 0.136-0.291 L/m2 |
| Thickness | Wet film 136–291 µm, dry film 75–160 µm |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 8 h | 5 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 48 h | 36 h | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | BANNOH 500 R, SILVAX SQ-K and other products |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6. Slight colour change may occur after immersion and outdoor exposure.
7. Density, solids content and VOC are calculated values without added thinner. They vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.