5906 SEA GRANDPRIX 500 HS Self-polishing Antifouling belongs to Antifouling. Good antifouling performance comes from highly active polymers, which ensure high efficacy and release of biocides. Parameters on this page: volume solids 52 ± 2%, dry film thickness 40–150 µm, theoretical spreading rate 0.077–0.288 L/m². Comparable products of the same brand and type: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling.
Parameter source: CMP original technical data sheet (TDS) '5906 SEA GRANDPRIX 500 HS Self-polishing Antifouling'; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 52 ± 2% |
|---|---|
| Dry Film Thickness | 40–150 µm |
| Theoretical Spreading Rate | 0.077-0.288 L/m2 |
| VOC | 452 g/L |
| Density / Specific Gravity | 1.86g/ml |
| Number of Components | One-component |
| Flash Point | 25°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red, light red, purple, red N, light red N |
SEA GRANDPRIX 500 HS is a tin-free self-polishing antifouling based on special resins with high hydrolysis activity.
Good antifouling performance derives from the highly active polymer, which ensures high efficacy and release of the biocide.
Provides long-term antifouling protection through a controlled hydrolysis maintaining surface activity.
The product complies with the IMO Antifouling System Convention (AFS/CONF/26).
| Type | Self-polishing Antifouling |
|---|---|
| Use | Suitable as a bottom antifouling for ocean-going steel ships to extend docking intervals. |
| Colour | Red, light red, purple, red N, light red N |
|---|---|
| Flash Point | 25°C |
| Density | 1.86g/ml |
| Volume Solids | 52 ± 2% |
| Volatile organic compound content | 452 g/L |
| Theoretical spreading rate | 0.077-0.288 L/m2 |
| Thickness | WFT 77–288 µm, DFT 40–150 µm |
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 6 h | 4 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 48 h | 36 h | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | SILVAX SQ-K, RAVAX AC-HB, BANNOH 500 N, BANNOH 500 R, BANNOH 500 S, etc. |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. If a ship berths continuously for two weeks or longer, especially in areas at risk of heavy marine growth, the bottom antifouling areas may be fouled by marine organisms.
2 Below 10 °C, additional thinner may be required to obtain suitable application viscosity.
3 However, adding too much thinner will reduce sag resistance and film performance.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.