5905 SEA GRANDPRIX 500 Tin-free Self-polishing Antifouling Paint is an antifouling coating. SEA GRANDPRIX 500 is a tin-free self-polishing antifouling paint based on a special resin with high hydrolysis activity. Parameters on this page: volume solids 46 ± 2% (by volume) (ISO 3233); dry film thickness 50–150 µm; theoretical spreading rate 0.109–0.326 L/m². Comparable products from the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling Paint, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling Paint, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling Paint.
Source: CMP original technical data sheet (TDS) '5905 SEA GRANDPRIX 500 Tin-free Self-polishing Antifouling Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 46 ± 2% (by volume) (ISO 3233) |
|---|---|
| Dry Film Thickness | 50–150 µm |
| Theoretical Spreading Rate | 0.109-0.326 L/m2 |
| VOC | 487 g/L (Method 24) |
| Density / Specific Gravity | 1.83g/ml (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 25°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red, light red, purple |
SEA GRANDPRIX 500 is a tin-free self-polishing antifouling paint based on a special resin with high hydrolysis activity.
The highly active resin ensures the most effective release of biocide, giving good antifouling performance.
Surface activity is controlled by hydrolysis, and the applied film thickness ensures long-term self-polishing protection.
The product complies with the IMO Antifouling System Convention (AFS/CONF/26).
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | Suitable as a bottom antifouling for ocean-going steel ships to extend docking intervals. |
| Colour | Red, light red, purple |
|---|---|
| Flash Point | 25°C |
| Density | 1.83g/ml (ISO: 2811) |
| Volume Solids | 46 ± 2% (by volume) (ISO 3233) |
| Volatile organic compound content | 487 g/L (Method 24) |
| Theoretical spreading rate | 0.109 - 0.326 L/m2 |
| Thickness | Wet film 109–326 µm; dry film 50–150 µm |
(dry film 100 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | |||
| Dry-to-launch time | Fastest | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | SILVAX SQ-K, RAVAX AC-HB, BANNOH 500 N, BANNOH 500 S, etc. |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
3. Adding too much thinner reduces sag resistance and drying performance.
4. Density, solids content and VOC content are measured without added thinner.
Values vary with colour or production process.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.