5844C SEAFLO NEO FLAT Tin-free Self-polishing Antifouling is an antifouling coating. SEAFLO NEO FLAT is a high-performance hydrolysing antifouling coating based on a hydrolysing polymer with low volatile organic compound content, ensuring long-term antifouling performance, low frictional resistance and low energy consumption. Parameters on this page: volume solids 60 ± 2% (volume) (ISO:3233); dry film thickness 75–150 µm; theoretical spreading rate 0.125–0.25 L/m². Comparable products of the same brand and category: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "5844C SEAFLO NEO FLAT Tin-free Self-polishing Antifouling"; values such as spreading rate are converted according to TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 2% (by volume) (ISO 3233) |
|---|---|
| Dry Film Thickness | 75–150 µm |
| Theoretical Spreading Rate | 0.125-0.25 L/m2 |
| VOC | 374 g/L |
| Density / Specific Gravity | 2.05 g/ml |
| Number of Components | One-component |
| Flash Point | 25.0°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red, light red |
SEAFLO NEO FLAT is a high-performance hydrolysing antifouling coating based on a hydrolysing polymer with low volatile organic compound content, ensuring long-term antifouling performance, low frictional resistance and low energy consumption. Compared with conventional hydrolysing paints, SEAFLO NEO FLAT has higher volume solids.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | An antifouling specifically for the flat bottoms of steel vessels. |
| Colour | Red, light red |
|---|---|
| Flash Point | 25.0°C |
| Density | 2.05 g/ml |
| Volume Solids | 60 ± 2% (by volume) (ISO 3233) |
| Volatile organic compound content | 374 g/L |
| Theoretical spreading rate | 0.125-0.25 L/m2 |
| Thickness | Wet film thickness 125–250 µm; dry film thickness 75–150 µm. |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 8 h | 5 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 24 h | 18 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 24 h | 18 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 52 h | 40 h | 28 h | 20 h | 14 h | 12 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | BANNOH 500 N,BANNOH 500 R,BANNOH 500 S,CMP AC-10,SILVAX SQ-K,RAVAX AC-HBBANNOH 1500 N, BANNOH 1500 S |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. If a ship berths continuously for two weeks or longer, especially in areas at risk of heavy marine growth, the bottom antifouling areas may be fouled by marine organisms.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6 Slight colour variation may occur after immersion and natural exposure.
7 Density and volatile organic compound content are theoretical calculated values of the formulation for the typical colour (red) paint with no thinner added. Values differ for formulations of different colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.