5843N SEAFLO NEO SL Tin-free Self-polishing Antifouling belongs to antifouling coatings. SEAFLO NEO SL is a high-performance hydrolytic antifouling based on silane polymer, offering long-term antifouling performance, low friction resistance and low energy consumption. Parameters on this page: volume solids 56 ± 2% (by volume) (ISO: 3233), dry film thickness 75–165 µm, theoretical spreading rate 0.134–0.295 L/m². Comparable products of the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "5843N SEAFLO NEO SL Tin-free Self-polishing Antifouling"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 56 ± 2% (by volume) (ISO 3233) |
|---|---|
| Dry Film Thickness | 75–165 µm |
| Theoretical Spreading Rate | 0.134-0.295 L/m2 |
| VOC | 408 g/L (Method 24) |
| Density / Specific Gravity | 1.90 g/ml (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 23.2°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Brown H, light brown H |
SEAFLO NEO SL is a high-performance hydrolysable antifouling based on silane polymer, providing long-term antifouling performance, low frictional resistance and low energy consumption.
SEAFLO NEO SL has a higher solids content than conventional hydrolysable coatings.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | Suitable as a bottom antifouling for ocean-going steel ships to extend docking intervals. |
| Colour | Brown H, light brown H |
|---|---|
| Flash Point | 23.2°C |
| Density | 1.90 g/ml (ISO: 2811) |
| Volume Solids | 56 ± 2% (by volume) (ISO 3233) |
| Volatile organic compound content | 408 g/L (Method 24) |
| Theoretical spreading rate | 0.134-0.295 L/m2 |
| Thickness | WFT 134–295 µm, DFT 75–165 µm |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 8 h | 5 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 22 h | 16 h | 12 h | 8 h | 5 h | 4 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 48 h | 36 h | 24 h | 18 h | 12 h | 10 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | BANNOH 1500 N, BANNOH 1500 S, BANNOH 500 N, BANNOH 500 R, BANNOH 500 S, BANNOH 1500 R Z, SILVAX SQ-K, CMP AC, CMP AC-10, among others |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6. Slight colour change may occur after immersion and outdoor exposure.
7. Density, volume solids and VOC content are theoretical calculated values without thinner. Values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.