5843L SEAFLO NEO Z Tin-free Self-polishing Antifouling Paint is an antifouling paint. SEAFLO NEO Z is a high-performance hydrolysing antifouling paint based on a low-VOC hydrolysing polymer, ensuring long-lasting antifouling performance, low friction resistance and low energy consumption. Parameters on this page: volume solids 59 ± 2% (by volume), dry film thickness 75–160 µm, theoretical spreading rate 0.127–0.271 L/m². Comparable products of the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling Paint, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling Paint, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling Paint.
Data source: CMP original Technical Data Sheet (TDS), "5843L SEAFLO NEO Z Tin-free Self-polishing Antifouling Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 59 ± 2% (by volume) |
|---|---|
| Dry Film Thickness | 75–160 µm |
| Theoretical Spreading Rate | 0.127-0.271 L/m2 |
| VOC | 357 g/L |
| Density / Specific Gravity | 2.12 g/ml |
| Number of Components | One-component |
| Flash Point | 26°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Red N2, light red N2 |
SEAFLO NEO Z is a high-performance hydrolysing antifouling paint based on a low-VOC hydrolysing polymer, ensuring long-lasting antifouling performance, low friction resistance and low energy consumption. Compared with ordinary hydrolysing paints, SEAFLO NEO Z has a higher volume solids content.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | Can be used as an antifouling paint to extend the docking interval. |
| Colour | Red N2, light red N2 |
|---|---|
| Flash Point | 26°C |
| Density | 2.12 g/ml |
| Volume Solids | 59 ± 2% (by volume) |
| Volatile organic compound content | 357 g/L |
| Theoretical spreading rate | 0.127-0.271 L/m2 |
| Thickness | Wet film 127–271 µm, dry film 75–160 µm |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 8 h | 5 h | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 28 h | 20 h | 14 h | 10 h | 7 h | 6 h | |
| Recoat interval | At least | 28 h | 20 h | 14 h | 10 h | 7 h | 6 h |
| At most | / | / | / | ||||
| Dry-to-launch time | Fastest | 52 h | 40 h | 28 h | 20 h | 14 h | 12 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.5Pa·s |
| Nozzle | (Graco)619-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | BANNOH 1500 N, BANNOH 1500 S, BANNOH 500 N, BANNOH 500 R, BANNOH 500 S, SILVAX SQ-K, CMP AC, BANNOH 1500 N Z, BANNOH 1500 S Z, etc. |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Expected antifouling performance during berthing: consider the ship's operating conditions and the berthing environment, such as marine growth activity, pollution level and water temperature at the berth. For details, consult the local CMP office.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir with a mixer until homogeneous, then add the appropriate thinner and mix.
4. Below 10 °C, additional thinner may be required to obtain a suitable application viscosity.
5. Excessive thinning, however, reduces sag resistance and film performance.
6. Slight colour change may occur after immersion and outdoor exposure.
7. Density, solids content and VOC content are theoretical calculated values for a typical colour (brown), based on the formulation without added thinner. Values vary between colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.