4001 RAVAX AC HB Chlorinated Rubber Anti-corrosive Paint is a chlorinated rubber paint, used as a primer. It also has seawater resistance and, even after prolonged exposure to severe weather, maintains good compatibility with subsequently applied paints. Parameters on this page: volume solids 47 ± 2% (ISO: 3233), dry film thickness 40–75 µm, theoretical spreading rate 0.085–0.160 L/m². Comparable products of the same brand: 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Galvanized Steel Primer, 2131 ROSWAN QD HB High-build Special Alkyd Primer.
Data source: CMP original Technical Data Sheet (TDS), "4001 RAVAX AC HB Chlorinated Rubber Anti-corrosive Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 47 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 40–75 µm |
| Theoretical Spreading Rate | 0.085-0.160 L/m2 |
| VOC | 486 g/L (Method 24) |
| Density / Specific Gravity | 1.3 g/mL (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 27°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Silver-red, silver |
RAVAX AC HB is a chlorinated rubber coating that provides fast drying and overcoating and good anti-corrosion protection. It has good adhesion to shop primers and subsequently applied paints. It also has seawater resistance and, even after prolonged exposure to severe weather, maintains good compatibility with subsequently applied paints.
| Type | Chlorinated Rubber Anticorrosive |
|---|---|
| Use | Ship hull plating and other steel structures |
| Colour | Silver-red, silver |
|---|---|
| Flash Point | 27°C |
| Density | 1.3 g/mL (ISO: 2811) |
| Volume Solids | 47 ± 2% (ISO: 3233) |
| Volatile organic compound content | 486 g/L (Method 24) |
| Theoretical spreading rate | 0.085-0.160 L/m2 |
| Thickness | WFT 85–160 µm |
| Dry film | 40–75 µm |
( )
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1 h | 45 min | 30 min | 20 min |
| Hard Dry | 6 h | 4.5 h | 3 h | 2.5 h | |
| Recoat interval | At least | 12 h | 8 h | 6 h | 5 h |
At most
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 140 seconds (Ford Cup No. 4) |
| Nozzle | Graco721, 723 |
| Paint output pressure | 14.7-17.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–5% by volume |
| Preceding coat | NZ PRIMER, WELBOND, EPICON ZINC RICH PRIMER, CERABOND, etc. |
| Subsequent coat | RAVAX AF, RAVAX FINISH, TFA-10.20.30, etc. |
| Packaging | One-component |
Density, volume solids and VOC content are theoretical calculated values excluding thinner.
The values depend on the formulation of different colours and the production process, etc.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.