Epoxy Sealer ZD1035 is an epoxy coating used as a primer. Used for surface treatment of cement or concrete substrates before applying high-performance concrete coatings, providing a surface with anti-penetration, easy cleaning and good adhesion for subsequent coats. A two-component transparent epoxy sealer composed of epoxy resin, solvent, additives and amine curing agent. Parameters on this page: volume solids 37 ± 3%, dry film thickness 25/40/50 µm, theoretical spreading rate 0.127 kg/m². Comparable products from the same brand: ZD6310-N01P Epoxy Oil-resistant Antistatic Primer, ZD6317 Fast-drying Zinc Phosphate Epoxy, Epoxy Primer for Hot-dip Galvanising ZD6180.
Source: ZINDN original technical data sheet (TDS) "Epoxy Sealer ZD1035"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 37 ± 3% |
|---|---|
| Dry Film Thickness | 25/40/50 µm |
| Theoretical Spreading Rate | 0.127 kg/m² |
| VOC | ≤555g/L |
| Density / Specific Gravity | 0.94 ± 0.1 |
| Number of Components | Two-component |
| Flash Point | >25 °C (components A, B and the mixture) |
| Thinner | ZX-06 Epoxy Thinner |
| Mixing Ratio | Component A (base) : Component B (curing agent) = 1:1 |
ZD1035 Epoxy Sealer
A two-component transparent epoxy sealer composed of epoxy resin, solvent, additives and amine curing agent.
High penetration, ensuring good adhesion between the ZINDN series products and the substrate surfaces of most concrete, cement and masonry structures; after treatment with this product, the sealing and the adhesion of the composite coating to the substrate are improved.
For preparing cement or concrete substrates before applying high-performance concrete coatings, providing a surface with anti-penetration, easy cleaning and good adhesion for the subsequent coat.
| Colour | Clear |
|---|---|
| Gloss | |
| Volume Solids | 37±3% |
| Mixed density (kg/L) | 0.94±0.1 |
| Dry film thickness (µm) | Minimum 25 | Typical 40 | Maximum 50 |
| Wet film thickness (µm) | 91 | 152 | 242 |
| Theoretical spreading rate (kg/m²) | 0.063 | 0.102 | 0.127 |
Note: as a penetrating sealer, the final dry film thickness depends on the porosity and penetration of the substrate.
| Practical Spreading Rate | Allowing for a loss factor, the substrate porosity and surface roughness affect the practical spreading rate. |
|---|---|
| VOC content | ≤555g/L |
All cracks, joints, protrusions and depressions have been correctly treated.
Before application, treat the concrete surface using dust-free blasting equipment, rotary grinding tools, blasting or high-pressure water jetting to achieve a suitable surface roughness, vacuum up the dust, and keep the floor clean and dry.
The substrate temperature must not be below 5 °C and must be at least 3 °C above the air dew point. Temperature and relative humidity must be measured on the substrate near the work area.
Do not apply outdoors in adverse weather such as rain, fog, snow, strong wind and heavy dust;
| Mixing | This product is supplied as two containers forming one unit. Stir the base thoroughly with a power mixer, add the curing agent in the specified ratio, stir again with a power mixer, and add the recommended thinner to adjust to a suitable application viscosity. Once mixed, use within the specified pot life. |
|---|---|
| Thinner / Cleaning Solvent | ZX-06 Epoxy Thinner |
| Mixing ratio (by weight) | Component A (base) : Component B (curing agent) = 1:1 |
| Induction Time | 20 min (25 °C) |
| 5°C | 15°C | 25°C | 35°C |
| 6 h | 5 h | 4 h | 3 h |
| Application Methods | Airless spray is recommended; air spray is not recommended; brush and roller are recommended only for touch-up, small-area application or repair. |
|---|
| Application Methods | Unit | High-pressure airless spray | Brush/roller |
| Spray gun tip size | mm | 0.43~0.53 | —— |
| Spray pressure | kg/cm² | 150~200 | —— |
| Thinning quantity | % | 0~10 | 5~10 |
| Substrate surface temperature | 5°C | 15°C | 25°C | 35°C |
| Touch Dry | 4 h | 2 h | 1 h | 0.5 h |
| Hard Dry | 24 h | 12 h | 8 h | 4 h |
| Minimum recoat interval | 16 h | 8 h | 4 h | 2 h |
| Maximum recoat interval | 7 days | 5 days | 3 days | 2 days |
Note: the above data are measured under well-ventilated conditions, at typical film thickness and 75% relative humidity, and are for reference only.
Actual drying times and the interval before recoating may be longer or shorter depending on film thickness, ventilation, humidity, the underlying paint, requirements for early handling and mechanical strength, and other factors.
| Preceding coat | None |
|---|---|
| Subsequent coat | Epoxy resin coating, epoxy intermediate coat, polyurethane coating |
If the substrate is heavily porous, apply several coats to fully seal the surface and avoid bubbles and pinholes when applying the next coat.
| Packaging Specifications | Component A 16 kg, Component B 16 kg |
|---|---|
| Flash Point | >25 °C (components A, B and the mixture) |
| Storage conditions | Store in accordance with national regulations. Keep in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. |
| Shelf life | Shelf life is 1 year under good storage conditions. |
This product contains flammable materials; site safety must comply with the relevant national or local regulations. Read the safety labels on the packaging and the product Safety Data Sheet (MSDS).
Avoid inhaling solvent vapours and spray mist, avoid contact of paint with skin and eyes, and do not swallow the product. Take the necessary precautions and protective measures for fire prevention, explosion prevention and environmental protection. Use only in well-ventilated conditions. In confined or poorly ventilated areas, provide forced ventilation.
Waste disposal must comply with the relevant national or local regulations.
The information and data in this document are accumulated from our tests and practical experience and may serve as an application guide. Since the use of the product is generally beyond our control, we guarantee only the quality of the product itself. We reserve the right to modify this document without prior notice as the product is improved.
| Version information | Published in July 2020; this data sheet supersedes all previous versions |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.