Epoxy Glass Flake Paint XH4011 belongs to glass flake paints and the epoxy paint system. It can be used as a primer, intermediate coat, topcoat, or single-coat system in atmospheric and highly corrosive environments, providing long-term anti-corrosion protection. Parameters on this page: volume solids 80 ± 2%, DFT 100/200/300 µm, theoretical spreading rate 2.6 m²/L.
Parameter source: T&H original technical data sheet (TDS) "Epoxy Glass Flake Paint XH4011"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 80 ± 2% |
|---|---|
| Dry Film Thickness | 100/200/300 µm |
| Theoretical Spreading Rate | 2.6 m2/L |
| VOC | 200g/L |
| Density / Specific Gravity | 1.35 kg/L |
| Number of Components | Two-component |
| Flash Point | 25°C |
| Thinner | 5-15% |
| Mixing Ratio | Base : curing agent = 10:1 (by weight), 87:13 (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A high-solids, high-build, two-component epoxy coating. It contains a large amount of chemical-resistant glass flake and provides high corrosion resistance, chemical resistance, and abrasion resistance. It can be used as a primer, intermediate coat, topcoat, or single-coat system in atmospheric and highly corrosive environments, providing long-term anti-corrosion protection.
| Colour | Grey, or other colours within a limited range |
|---|---|
| Gloss | N/A |
| density | 1.35 kg/L |
| Volume Solids | 80±2% |
| Volatile Organic Compounds | 200g/L |
| Flash Point | 25°C |
| Mixing ratio | Base : curing agent = 10:1 (by weight), 87:13 (by volume) |
| Typical dry film thickness | 200µm |
|---|---|
| Recommended dry film thickness | 100–300 µm, depending on system requirements |
| Induction time (20 °C) | 10~15min |
| Thinner quantity (by volume) | Airless spray 0–15% | Air spray 5–20% | Roller or brush 5–15% |
| Recommended nozzle size | 0.43~0.64mm | 1.5~2.5mm | / |
| Recommended spray pressure | 15~20MPa | 0.3~0.6MPa | / |
| Application suitability | Recommended | Applicable | For small-area repair only |
*Use a slow thinner in hot weather
| Dry film thickness (µm) | 100 | 200 | 300 |
| Wet film thickness (µm) | 125 | 250 | 375 |
| Theoretical spreading rate (m²/L) | 7.8 | 3.9 | 2.6 |
| Temperature | Surface Dry | Hard Dry | Pot Life | Recoat interval | |
| Minimum | Maximum* | ||||
| 5°C | 120min | 24h | 6h | 24h | / |
| 15°C | 90min | 20h | 4h | 24h | / |
| 25°C | 60min | 12h | 4h | 12h | / |
| 40°C | 45min | 6h | 2h | 8h | / |
*The maximum recoat interval depends on the exposure environment and the end use of the coating.
All surfaces to be coated must be clean, dry and free of contaminants. Before application, all surfaces must be assessed and prepared in accordance with ISO 8504:2000. Abrasive blast clean to Sa 2½, with surface roughness 40–75 µm. Before rust removal, remove all oil and weld spatter and grind welds and sharp edges. Areas of the coating damaged mechanically and showing localised rust must be spot blast cleaned to Sa 2½ or cleaned with power tools to St 3 before local repair. If this coating is to be applied over an approved zinc dust primer old film, thoroughly remove any chalking or zinc salts from the zinc dust coating before applying this product. For concrete protection, the concrete must be cured, with moisture content and surface condition meeting the relevant requirements.
1 Ensure ventilation and exhaust during application, keep away from ignition sources, and wear protective equipment such as masks and gloves. Maintain adequate ventilation during curing. 2 Before mixing Components A and B, stir the base thoroughly with a power tool, then add the hardener and mix uniformly. Adjust thinner addition according to application requirements and temperature changes, mix thoroughly, and allow an induction time of 10–15 min before application. 3 The product can be used as a primer for galvanized steel or stainless steel. Roughening by grinding or light blasting of these substrate surfaces can improve adhesion. 4 When used as a protective primer for concrete, it is usually used with a dedicated concrete sealer primer to seal the concrete. Ensure the sealer is hard dry before applying subsequent coats. 5 If this coating is to be applied over old zinc-rich primer films, powdery degradation or zinc salts on the zinc-rich coating must be thoroughly removed. 6 The recommended thickness per coat of this product shall not exceed 200 µm. If chalking occurs after long-term exposure of the coating, clean with high-pressure water or abrade the surface before applying subsequent coats. 7 During application and curing, substrate temperature must be above 5°C and at least 3°C above the dew point, and relative humidity shall not exceed 85%. Temperature and relative humidity shall be measured at the substrate near the work area. 8 Cutting structures coated with this product generates smoke and dust; appropriate protection shall be provided. 9 When work is suspended, do not leave paint in paint hoses, spray guns, or spray equipment. Thoroughly flush all equipment with thinner. If the suspension is prolonged, it is recommended to mix a new batch of paint for application. 10 All equipment shall be cleaned with thinner immediately after use. Periodic flushing of spray equipment during daily work is good practice. Cleaning frequency depends on spray volume, temperature, spray time, including interruption time. 11 Residual paint and empty cans shall be disposed of in accordance with relevant local regulations.
| 23.1 kg per unit | Base 21 kg | Curing agent 2.1 kg |
| 17 L per set | Base 14.8 L | Curing agent 2.2 L |
Keep sealed in a ventilated, cool, dry place away from sources of ignition. Minimum 12 months.
1. For the coating and its recommended thinners, see the safety sheets and the safety data of the relevant materials. This is a solvent-borne coating; avoid inhaling spray mist and solvent vapours, and avoid exposing skin and eyes and contact with uncured paint as far as possible. 2. All work related to the application and use of this product must comply with the relevant national health, safety and environmental standards and regulations. 3. If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation. 4. If in doubt about the suitability of this product, consult the company.
The information provided in this product data sheet is based on laboratory test results that we consider accurate, and is provided for application guidance only. All recommendations and advice given by T&H on the use of T&H products, whether in technical documents, special consultation or otherwise, are based on information we consider most reliable. Our products and the information provided are intended for users with the necessary knowledge and industrial experience, and it is for these end users to determine whether the products are suitable for their use. T&H cannot control the quality and condition of the substrate, nor the various factors affecting the use of the product. Therefore, T&H accepts no liability for any loss, injury or damage arising from the use of our products or from reliance on this product data sheet (unless otherwise agreed in writing). Data in this product data sheet may be revised as necessary based on practical experience and continued product development.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.