Inorganic Zinc-rich Primer XH4008 is a zinc-rich primer. It is used for the protection of steel facilities and equipment, high-temperature pipelines, bridges, storage tanks, etc. in severe atmospheric corrosive environments. Parameters on this page: volume solids 61 ± 2%, dry film thickness 60/80/100 µm, theoretical spreading rate 6.1 m²/L.
Parameter source: T&H manufacturer's Technical Data Sheet (TDS) "Inorganic Zinc-rich Primer XH4008"; spreading rate and other values are converted from the TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 61 ± 2% |
|---|---|
| Dry Film Thickness | 60/80/100 µm |
| Theoretical Spreading Rate | 6.1 m2/L |
| VOC | 440g/L |
| Density / Specific Gravity | 3.1 kg/L |
| Number of Components | Two-component |
| Flash Point | 17°C |
| Thinner | 5-15% |
| Mixing Ratio | Base : curing agent = 4.3:1 (by weight), 39:61 (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Two-component solvent-borne inorganic zinc silicate coating; performance and composition comply with the requirements of HG/T3668. Used for the protection of steel facilities and equipment, high-temperature pipelines, bridges, storage tanks, etc. in severe atmospheric corrosive environments.
| Colour | Zinc grey |
|---|---|
| Gloss | N/A |
| density | 3.1 kg/L |
| Volume Solids | 61±2% |
| Volatile Organic Compounds | 440g/L |
| Flash Point | 17°C |
| Mixing ratio | Base : curing agent = 4.3:1 (by weight), 39:61 (by volume) |
| Typical dry film thickness | 60µm |
|---|---|
| Recommended dry film thickness | 50–100 µm, depending on system requirements |
| Induction time (20 °C) | No induction required |
| Thinner quantity (by volume) | Airless spray 5–20% | Air spray 5–20% | Roller or brush 5–15% |
| Recommended nozzle size | 0.43~0.64mm | 2.0~3.0mm | / |
| Recommended spray pressure | 15~20MPa | 0.3~0.6MPa | / |
| Application suitability | Recommended | Applicable | Suitable for small-area repair |
*For low-temperature application and where fast hard drying is required, use a fast thinner.
| Dry film thickness (µm) | 60 | 80 | 100 |
| Wet film thickness (µm) | 100 | 130 | 160 |
| Theoretical spreading rate (m²/L) | 10.2 | 7.6 | 6.1 |
Application data (typical dry film thickness 60 µm, 65% relative humidity):
| Temperature | Surface Dry | Hard Dry | Pot Life | Recoat interval | |
| Minimum | Maximum* | ||||
| 5°C | 60min | 12h | 8h | 48h | / |
| 15°C | 60min | 6h | 48h | / | |
| 25°C | 30min | 4h | 5h | 24h | / |
| 40°C | 30min | 2h | 3h | 24h | / |
*The maximum recoat interval depends on the exposure environment and the end use of the coating.
All surfaces to be coated must be clean, dry and free of contaminants. Before application, all surfaces must be assessed and prepared in accordance with ISO 8504:2000
assessed and prepared in accordance with. Abrasive blast clean to Sa 2½, with surface roughness 40–75 µm. Before rust removal, remove all oil and weld spatter and grind welds and sharp edges. Areas of the coating damaged mechanically and showing localised rust must be spot blast cleaned to Sa 2½ or cleaned with power tools to St 3 before local repair with this primer. If the old film shows chalking or zinc salts, remove the zinc salts and contaminants before applying another primer, intermediate coat or topcoat.
1. During application, ensure ventilation and exhaust, keep away from ignition sources, and wear protective equipment such as masks and gloves; maintain adequate ventilation during curing. 2. Slowly add the zinc powder component to the liquid component under agitation, and mix thoroughly with a power tool; adjust the thinner amount according to application needs and temperature changes, and mix thoroughly; it is recommended to filter through a 120-mesh screen before use and to maintain continuous agitation during use. If the zinc powder is poured directly into the liquid component, or if thinner is added before mixing, the paint will be difficult to mix uniformly, and defects such as gun clogging and uneven film may easily occur. 3. The maximum permitted coating film thickness for this product is 120 µm; excessive thickness may cause cracking. During application, pay attention to the treatment of edges and corners of the coated component and to excessive coating thickness to avoid cracking. 4. This product is only suitable for application on blast-cleaned steel surfaces and inorganic zinc silicate coating surfaces, and shall not be applied over other types of coatings. Substrate surfaces with excessively low roughness or smooth surface coatings cannot achieve good adhesion and may even peel off. 5. During application and curing, the substrate temperature must be above 5 °C and at least 3 °C above the dew point, and the relative humidity shall not exceed 85%. Temperature and relative humidity shall be measured at the substrate near the work site. Maintain good ventilation in the application environment, with relative humidity not lower than 60%. If the humidity during actual application is below 60%, water spraying for humidification is required, and before recoating, the degree of cure shall be assessed in accordance with ASTM D4752, reaching at least grade 4. 6. When the product is used alone in systems resistant to oils, solvents and chemicals, the coating thickness shall not exceed 90 µm. The permissible pH range of the medium is 6-9. Assess the degree of cure in accordance with ASTM D4752, reaching grade 5. 7. Cutting structures coated with this coating generates smoke and dust; appropriate protection shall be provided. 8. When applying other coatings over this product's coating, sealing treatment shall be carried out in advance; a dedicated sealer primer is recommended, or the subsequently applied epoxy coating may be thinned and mist-sprayed for sealing treatment to avoid blistering. Alkyd, alkyd-modified coatings, polyurethane coatings, etc. shall not be applied directly over this product's coating. 9. When work is suspended, do not leave paint in paint lines, spray guns or spray equipment. Thoroughly flush all equipment with thinner. If the suspension is too long, it is recommended to mix a new batch of paint for application. 10. All equipment shall be cleaned with thinner immediately after use. Periodically flushing spray equipment during daily work is a good practice. Cleaning frequency depends on spray volume, temperature, spray time, including interruption time and other factors. 11. Residual paint and empty cans shall be disposed of in accordance with relevant regional regulations.
| 25.4 kg per unit | Base 20.6 kg | Curing agent 4.8 kg |
| 8.2 L per set | Base 3.2 L | Curing agent 5 L |
Keep sealed in a ventilated, cool, dry place away from sources of ignition. Minimum 9 months.
1. For the coating and its recommended thinners, see the safety sheets and the safety data of the relevant materials. This is a solvent-borne coating; avoid inhaling spray mist and solvent vapours, and avoid exposing skin and eyes and contact with uncured paint as far as possible. 2. All work related to the application and use of this product must comply with the relevant national health, safety and environmental standards and regulations. 3. If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation. 4. If in doubt about the suitability of this product, consult the company.
The information provided in this product data sheet is based on laboratory test results that we consider accurate, and is provided for application guidance only. All recommendations and advice given by T&H on the use of T&H products, whether in technical documents, special consultation or otherwise, are based on information we consider most reliable. Our products and the information provided are intended for users with the necessary knowledge and industrial experience, and it is for these end users to determine whether the products are suitable for their use. T&H cannot control the quality and condition of the substrate, nor the various factors affecting the use of the product. Therefore, T&H accepts no liability for any loss, injury or damage arising from the use of our products or from reliance on this product data sheet (unless otherwise agreed in writing). Data in this product data sheet may be revised as necessary based on practical experience and continued product development.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.