NavalGuard5407 alkyd primer is an alkyd coating used as a primer for short-term protection in low to moderate corrosivity environments. Parameters on this page: volume solids 55 ± 2%, dry film thickness 40/60/80 µm, theoretical spreading rate 6.6 m²/L.
Parameter source: T&H original technical data sheet (TDS) for Water Shield Alkyd Primer NavalGuard5407; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 55 ± 2% |
|---|---|
| Dry Film Thickness | 40/60/80 µm |
| Theoretical Spreading Rate | 6.6 m2/L |
| VOC | 420g/L |
| Density / Specific Gravity | 1.8 kg/L |
| Number of Components | One-component |
| Flash Point | 25°C |
| Thinner | 5-15% |
| Colour / Appearance | Iron red/grey |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Curing agent: none
A single-component, fast-drying alkyd primer for short-term protection in low to medium corrosive environments.
| Colour | Iron red/grey |
|---|---|
| Gloss | N/A |
| density | 1.8 kg/L |
| Volume Solids | 55±2% |
| Volatile Organic Compounds | 420g/L |
| Flash Point | 25°C |
| Typical dry film thickness | 60µm |
|---|---|
| Recommended dry film thickness | 40–80 µm, depending on system requirements |
| Thinner quantity (by volume) | Airless spray 5–15% | Air spray 10–30% | Roller or brush 5–15% |
| Recommended nozzle size | 0.43~0.64mm | 1.5~2.5mm | / |
| Recommended spray pressure | 15~20MPa | 0.3~0.6MPa | / |
| Application suitability | Recommended | ||
| Dry film thickness (µm) | 40 | 60 | 80 |
| Wet film thickness (µm) | 73 | 109 | 145 |
| Theoretical spreading rate (m²/L) | 13.2 | 8.8 | 6.6 |
| Temperature | Surface Dry | Hard Dry | Pot Life | Recoat interval | |
| Minimum | Maximum* | ||||
| 5°C | 4h | 48h | / | 48h | / |
| 15°C | 3h | 36h | / | 36h | / |
| 25°C | 2h | 24h | / | 24h | / |
| 40°C | 1h | 16h | / | 16h | / |
*The maximum recoat interval depends on the exposure environment and the end use of the coating.
All surfaces to be coated shall be clean, dry and free from contaminants. Prior to coating, all surfaces shall be assessed and prepared in accordance with ISO 8504:2000. Abrasive blast cleaning to Sa2½ (ISO 8501-1:2007). If oxidation occurs between abrasive blast cleaning and application of this product, the surface shall be re-blasted to the specified visual standard. Surface defects revealed by the blast cleaning process shall be ground, filled or treated in an appropriate manner. This product is suitable for application on surfaces that have been abrasive blast cleaned to the above standard and then naturally degraded for no more than 7–10 days under good shop conditions.
surface. Where the coating film has suffered mechanical damage with localised rusting, it shall be abraded, filled or otherwise treated. The surface quality may be reduced to Sa2, but loose powdery deposits shall not be present.
1. During application, ensure ventilation and exhaust, keep away from sources of ignition, and wear protective equipment such as a mask and gloves; maintain adequate ventilation also during curing. 2. Adjust the thinner quantity according to temperature, mix thoroughly, and filter through a 120-mesh copper screen before use. Seal unused paint if not used for a long time, otherwise skinning occurs; if skinning occurs, remove the skin before use. 3. The recommended dry film thickness per coat should not exceed 50 µm. Over-application in one coat affects curing and recoatability, and may cause lifting and wrinkling on recoating. This coating must not be applied over zinc-containing coatings, nor over hot-dip galvanised, hot-sprayed zinc or aluminium surfaces, otherwise adhesion is lost. 4. During application and curing, the substrate temperature must be above 5 °C and at least 3 °C above the dew point, with relative humidity not more than 85%. Temperature and relative humidity must be measured on the substrate near the work area. 5. Cutting of structures coated with this product produces fume; take appropriate protection. 6. When work is interrupted, do not leave paint in hoses, spray guns or spray equipment. Flush all equipment thoroughly with thinner. 7. Clean all equipment immediately after use with thinner. Flushing spray equipment periodically during daily work is good practice. Cleaning frequency depends on the volume sprayed, temperature, spraying time, including interruptions, and other factors. 8. Surplus paint and empty containers must be disposed of in accordance with the relevant regional regulations.
27kg/15L
Keep sealed in a ventilated, cool, dry place away from sources of ignition. Minimum 12 months.
1. For the coating and its recommended thinners, see the safety sheets and the safety data of the relevant materials. This is a solvent-borne coating; avoid inhaling spray mist and solvent vapours, and avoid exposing skin and eyes and contact with uncured paint as far as possible. 2. All work related to the application and use of this product must comply with the relevant national health, safety and environmental standards and regulations. 3. If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation. 4. If in doubt about the suitability of this product, consult the company.
The information provided in this product data sheet is based on laboratory test results that we consider accurate, and is provided for application guidance only. All recommendations and advice given by T&H on the use of T&H products, whether in technical documents, special consultation or otherwise, are based on information we consider most reliable. Our products and the information provided are intended for users with the necessary knowledge and industrial experience, and it is for these end users to determine whether the products are suitable for their use. T&H cannot control the quality and condition of the substrate, nor the various factors affecting the use of the product. Therefore, T&H accepts no liability for any loss, injury or damage arising from the use of our products or from reliance on this product data sheet (unless otherwise agreed in writing). Data in this product data sheet may be revised as necessary based on practical experience and continued product development.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.