Water Shield Pure Epoxy Coating NavalGuard4215 is an epoxy coating. A high-solids high-build epoxy coating used for corrosion protection of the interior walls of tanks and pipes for industrial wastewater, fire water and circulating water. Parameters on this page: volume solids 81 ± 2%, dry film thickness 80/150/200 µm, theoretical spreading rate 4 m²/L.
Parameter source: T&H original technical data sheet (TDS) for Water Shield Pure Epoxy Coating NavalGuard4215; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 81 ± 2% |
|---|---|
| Dry Film Thickness | 80/150/200 µm |
| Theoretical Spreading Rate | 4 m2/L |
| VOC | 190g/L |
| Density / Specific Gravity | 1.5kg/L |
| Number of Components | Two-component |
| Flash Point | 25°C |
| Thinner | 0-15% |
| Mixing Ratio | Base : curing agent = 6:1 (by weight), 79:21 (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A high-solids, high-build epoxy coating for the corrosion protection of the inner walls of tanks and pipelines for industrial waste water, fire-fighting water, circulating water and the like
| Colour | White, light grey, light pink |
|---|---|
| Gloss | N/A |
| density | 1.5kg/L |
| Volume Solids | 81±2% |
| Volatile Organic Compounds | 190g/L |
| Flash Point | 25°C |
| Mixing ratio | Base : curing agent = 6:1 (by weight), 79:21 (by volume) |
| Typical dry film thickness | 100µm |
|---|---|
| Recommended dry film thickness | 100–450 µm, depending on system requirements |
| Induction time (20 °C) | 10~15min |
| Thinner quantity (by volume) | Airless spray 0–10% | Air spray 5–20% | Roller or brush 0–15% |
| Recommended nozzle size | 0.43~0.64mm | 2.0~3.0mm | None |
| Recommended spray pressure | 15~20MPa | 0.3~0.6MPa | None |
| Application suitability | Recommended | Applicable | Suitable for small-area repair |
| Dry film thickness (µm) | 80 | 150 | 200 |
| Wet film thickness (µm) | 100 | 188 | 250 |
| Theoretical spreading rate (m²/L) | 9.9 | 5.3 | 4 |
| Temperature | Surface Dry | Hard Dry | Pot Life | Recoat interval | |
| Minimum | Maximum* | ||||
| 5°C | 4h | 24h | 4h | 24h | / |
| 15°C | 3h | 20h | 3h | 24h | / |
| 25°C | 1.5h | 12h | 1.5h | 12h | / |
| 40°C | 1h | 6h | 40min | 8h | / |
*The maximum recoat interval depends on the exposure environment and the end use of the coating.
All surfaces to be coated must be clean, dry and free of contaminants. Before application, all surfaces must be assessed and prepared in accordance with ISO 8504:2000. Areas of the coating damaged mechanically and showing localised rust must be spot blast cleaned to Sa 2½ or cleaned with power tools to St 3 before local repair. When applied over other existing coatings, remove chalk, zinc salts, grease and other contaminants by suitable methods. When applied over inorganic zinc silicate primers or metal spray surfaces, use an approved tie coat or transitional coat.
1. During application, ensure good ventilation and exhaust, keep away from ignition sources, and wear a mask, gloves and other protective equipment; adequate ventilation shall also be maintained during curing. 2. When mixing, first stir the base thoroughly, then add the curing agent in the specified ratio and mix uniformly; adjust the thinner amount according to application requirements and temperature changes, and mix and induce thoroughly. 3. When applied over inorganic zinc silicate coatings, a tie-coat shall be used for sealing; the product shall be applied only after the tie-coat is hard dry, otherwise the effectiveness of sealing pinholes will be reduced. 4. Excessive thinning will reduce sag resistance and slow curing. 5. Over-thick application will seriously affect drying, curing, overcoating performance and handling time. For better coating performance, when the film thickness exceeds 200 µm, apply in multiple coats to improve film density. Avoid over-thick application in a single pass on edges, corners, welds and similar areas; where these areas have been over-applied, the overcoating interval of subsequent coats shall be extended to allow solvent release, otherwise the coating may crack in service. 6. If the coating chalks after long-term exposure, wash with high-pressure water or abrade the surface before applying the next coat. 7. With roller application, high film thickness and a good continuous film cannot be obtained in a single pass; multiple coats are required. 8. During application and curing, the substrate temperature shall be above 5 °C and at least 3 °C above the dew point, and the relative humidity shall not exceed 85%. Good resistance to liquid media is achieved only after full cure of the film; the degree of cure depends on temperature, humidity and film thickness. At 25 °C and 50% humidity, a 200–300 µm coating requires at least 7–10 days of conditioning before contact with liquid media; as the temperature drops or the film thickness increases, the conditioning time shall be extended. At 10–15 °C, the coating requires at least 21 days of conditioning before service. Do not apply the product below 5 °C. 9. Cutting structures coated with this coating produces fumes; appropriate protection shall be taken. 10. When work is interrupted, do not leave paint in hoses, spray guns or spray equipment. Flush all equipment thoroughly with thinner. If work is interrupted for too long, remix a fresh batch of paint before resuming. 11. All equipment shall be cleaned with thinner immediately after use. Periodically flushing spray equipment during the daily work is good practice. The frequency of cleaning depends on the quantity sprayed, temperature, spraying time and interruptions. 12. Remaining paint and empty cans shall be disposed of in accordance with relevant local regulations.
| 24.5 kg per unit | Base 21 kg | Curing agent 3.5 kg |
| 16 L per unit | Base 12.7 L | Curing agent 3.3 L |
Keep sealed in a ventilated, cool, dry place away from sources of ignition. Minimum 12 months.
1. For the coating and its recommended thinners, see the safety sheets and the safety data of the relevant materials. This is a solvent-borne coating; avoid inhaling spray mist and solvent vapours, and avoid exposing skin and eyes and contact with uncured paint as far as possible. 2. All work related to the application and use of this product must comply with the relevant national health, safety and environmental standards and regulations. 3. If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation. 4. If in doubt about the suitability of this product, consult the company.
The information provided in this product data sheet is based on laboratory test results that we consider accurate, and is provided for application guidance only. All recommendations and advice given by T&H on the use of T&H products, whether in technical documents, special consultation or otherwise, are based on information we consider most reliable. Our products and the information provided are intended for users with the necessary knowledge and industrial experience, and it is for these end users to determine whether the products are suitable for their use. T&H cannot control the quality and condition of the substrate, nor the various factors affecting the use of the product. Therefore, T&H accepts no liability for any loss, injury or damage arising from the use of our products or from reliance on this product data sheet (unless otherwise agreed in writing). Data in this product data sheet may be revised as necessary based on practical experience and continued product development.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.