SKSHU FFMW202 Water-borne Fluorocarbon Topcoat belongs to water-borne paints and is used as a topcoat. Gloss and colour retention, water resistance, oil resistance, impact resistance, abrasion resistance, strong adhesion. Parameters on this page: volume solids 44 ± 2%, DFT 40-80 µm, theoretical spreading rate 5.88 m²/kg.
Parameter source: SKSHU (3TREES) original technical data sheet (TDS) "SKSHU FFMW202 Water-borne Fluorocarbon Topcoat"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 44 ± 2% |
|---|---|
| Dry Film Thickness | 40–80 µm |
| Theoretical Spreading Rate | 5.88 m²/Kg |
| VOC | <200 g/L |
| Density / Specific Gravity | Approx. 1.26 kg/L (varies slightly with colour) |
| Number of Components | Two-component |
| Thinner | Water |
| Mixing Ratio | FFMW202A (main paint):FFMW202B (curing agent) = 7.2 : 1... |
| Colour / Appearance | White, custom colours |
SKSHU FFMW202 Water-borne Fluorocarbon Topcoat
SKSHU FFMW202 is an ambient-curing, two-component, water-borne fluorocarbon resin coating composed of aliphatic isocyanate, hydroxyl-containing fluorocarbon resin, weather-resistant pigments and additives. As a protective and decorative topcoat, it is suitable for large machine tools, machinery, construction machinery, and agricultural machinery.
Low VOC, environmentally friendly; high gloss, fullness, good levelling; gloss and colour retention, water resistance, oil resistance, impact resistance, abrasion resistance, strong adhesion.
| Colour: | White, custom colours |
|---|---|
| Gloss: | High gloss (≥80°, 60°) |
| Volume solids: | 44±2% |
| Specific gravity: | Approx. 1.26 kg/L (varies slightly with colour) |
| Theoretical spreading rate: | 5.88 m²/kg, DFT 60 (µm) |
| Flash point: | Water-borne, not applicable |
| VOC content: | <200 g/L |
| Storage time: | Dry, cool environment, 6 months |
| Mixing ratio: | FFMW202A (main paint):FFMW202B (curing agent) = 7.2 : 1 (by volume) |
|---|---|
| Thinner | Water |
| Recommended dry film thickness: | 40~80 µm |
| Induction time: | No induction required |
Recommended amount of dilution water: as appropriate* (by weight)
| Airless Spray | Air Spray | Roller or brush | |
| As required* | |||
| Recommended nozzle size | 0.43mm | 1.5mm | / |
| Recommended spray pressure | 15-25MPa | 0.4-0.6MPa | / |
| Application suitability | Recommended | Applicable | Repair |
*Addition of dilution water improves application viscosity; for spraying, the amount added is based on satisfactory gun adjustment testing. Airless spray is preferred for this product; roller and brush application are suitable only for small-area repair. Theoretical consumption*
| Dry film thickness (µm) | 40 | 60 | 80 |
| Theoretical spreading rate (L/m²) | 0.09 | 0.14 | 0.18 |
| Theoretical spreading rate (kg/m2) | 0.12 | 0.17 | 0.23 |
Recoat time* Temperature
| 5°C | Minimum (h) 36 | Maximum (days) 7 |
| 10°C | 24 | 7 |
| 20°C | 12 | 7 |
| 30°C | 6 | 7 |
| *The recoat interval depends on the subsequent exposure conditions | If the maximum overcoating interval is exceeded, abrade the primer surface to ensure intercoat adhesion. Surfaces used in contaminated environments shall be washed clean with high-pressure fresh water or wiped with thinner and allowed to dry before overcoating. |
|---|
| Temperature | Touch dry (h) | Hard dry (days) | Pot life (h) |
| 5°C | 8 | 7 | 4 |
| 10°C | 4 | 3 | |
| 20°C | 1 | 2 | |
| 30°C | 0.5 | 1 |
- Adequate and continuous ventilation must be maintained during application and curing of the coating.
- When applying at ambient air or substrate surface temperatures below 5 °C, pre-warm the mixed paint to above 10 °C.
Where in direct contact with the substrate, all surfaces to be coated shall be clean, dry and free from contamination. Before painting, all surfaces shall be assessed and prepared in accordance with ISO 8501. Blast clean to Sa2½ with a surface profile of 40–75 µm. Before derusting, remove all oil, grease and weld spatter, and grind welds and sharp edges.
Areas that cannot be blasted must be cleaned with power tools to St 3, free of oil and water, with no loose material.
When the product is overcoated on other air-drying or chemically curing coatings, first confirm compatibility with the previous coat and check the overcoating interval of the previous coat. If the interval is exceeded, the previous coat shall be abraded, loose film removed by power tool, and other loose impurities removed; the surface shall be free of oil and water.
| FFM202A Water-borne Fluorocarbon Topcoat: | 22.22 kg/drum |
|---|---|
| FFM202B Water-borne Fluorocarbon Topcoat Curing Agent | 2.78 kg/drum |
This product is a water-borne, environmentally friendly coating; non-flammable and non-explosive.
The coating contains a water-borne co-solvent that may irritate the skin; wear a respirator and other protective equipment during application.
Do not inhale paint mist; avoid skin contact with the paint. Paint splashed on the skin shall be washed immediately with a suitable cleaning agent, soap and plenty of water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
Under normal application conditions, the coating dries. Detailed toxicity, safety and first-aid matters refer to the product's Safety Data Sheet (MSDS).
In all cases, SKSHU (3TREES) shall not be liable for any indirect, special, incidental or consequential loss of any kind arising from or in connection with the use of this product (whether based on negligence, strict liability or tort).
guidance. With accumulated experience and further product development, SKSHU may revise the above information at any time.
All recommendations and advice concerning the use of this product, whether in technical documents, in response to an enquiry or otherwise, are given to the best of our knowledge and are believed to be reliable. Our products and related information are provided for industrial users possessing the necessary knowledge and practical skills, and it is the end user's responsibility to determine whether the product is suitable for the specific use. The buyer, having performed such evaluation, proceeds entirely at its own risk.
The quality and condition of the substrate on site, and the many other factors affecting product use and application, are beyond SKSHU (3TREES)'s control.
SKSHU (3TREES) accepts no liability for coating quality problems caused by application environment, application process, surface preparation or personnel operation (unless otherwise provided in a written agreement).
To avoid misuse, confirm with our sales staff that the product data sheet in hand is the latest version.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.