SKSHU FFD033II Abrasion-Resistant Epoxy is an epoxy coating. It can cure at temperatures as low as -10 °C; the cured film has good abrasion resistance and excellent anticorrosive and mechanical properties. Parameters on this page: volume solids 77 ± 2%, dry film thickness 100-300 µm, theoretical spreading rate 5.12 m²/kg.
Parameter source: SKSHU (3TREES) original technical data sheet (TDS) for SKSHU FFD033II Abrasion-Resistant Epoxy; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 77 ± 2% |
|---|---|
| Dry Film Thickness | 100-300µm |
| Theoretical Spreading Rate | 5.12 m²/kg (100 µm dry film) |
| VOC | 211 g/L |
| Density / Specific Gravity | Approx. 1.50 kg/L |
| Number of Components | Two-component |
| Flash Point | 35°C |
| Thinner | FFX001 Epoxy Universal Thinner |
| Mixing Ratio | Base FFD033IIA : curing agent FFD033IIB = 4 : 1 (by volume… |
A high-solids, fast-curing two-component epoxy coating containing zinc phosphate pigment, with all-season application performance.
Particularly suitable for the protection of steel-structure workshops, municipal bridges, sports venues, and chemical and power/energy equipment and facilities.
May be used on various metal surfaces, such as iron-based, stainless steel and hot-dip galvanized surfaces.
Fast drying and fast overcoating, excellent anticorrosive performance, a long overcoating interval and flexible application.
Cures down to -10 °C; after curing, the film has good abrasion resistance and high anticorrosive and mechanical performance.
| Colour: | Grey |
|---|---|
| Gloss: | Flat |
| Volume solids: | 77±2% |
| Solids content by weight: | 88±2% |
| Theoretical spreading rate: | 5.12 m²/kg (100 µm dry film) |
| Specific gravity: | Approx. 1.50 kg/L |
| Flash point: | 35°C |
| VOC content: | 211 g/L |
| Fully cured | 7 days |
| Storage: | Dry, cool environment, 12 months |
| Mixing ratio: | Base FFD033IIA : curing agent FFD033IIB = 4 : 1 (by volume) |
|---|---|
| Thinner | FFX001 Epoxy Universal Thinner |
| Recommended dry film thickness: | 100-300µm |
| Thinner quantity | Airless spray 0–5%* | Air spray 0–5%* | Roller or brush 0–5%* |
| Recommended nozzle size | 0.43-0.48mm | 1.0-2.0mm | / |
| Recommended spray pressure | 15-25MPa | 0.3-0.6MPa | / |
| Application suitability | Recommended | Applicable | Repair |
*Adding thinner improves application viscosity; when spraying, add based on a satisfactory gun test, but the VOC emission requirements of national laws and regulations shall be met. Airless spray is the preferred method for this product; roller and brush are suitable only for small-area touch-up.
| Dry film thickness (µm) | 100 | 200 | 300 |
| Theoretical spreading rate m²/kg | 5.12 | 2.56 | 1.71 |
| Theoretical spreading rate m²/L | 7.70 | 3.85 | 2.57 |
Recoat time* Temperature
| -5°C | Minimum (h) 24 | Maximum (days) 60 |
| 0°C | 12 | 45 |
| 10°C | 8 | 30 |
| 20°C | 4 | 14 |
| 30°C | 2 | 7 |
| -- The recoat interval depends on the subsequent exposure conditions | If the maximum recoat interval is exceeded, abrade the primer surface to ensure intercoat adhesion. Surfaces exposed to a contaminated environment must be washed clean with high-pressure fresh water and allowed to dry before recoating. |
|---|
| Temperature | Touch dry (h) | Full cure (days) | Pot life (hours) |
| -5°C | 8 | 20 | N/A |
| 0°C | 5 | 14 | N/A |
| 10°C | 3 | 12 | 3 |
| 20°C | 2 | 7 | 2 |
| 30°C | 1 | 5 | 1 |
-- Adequate and continuous ventilation must be maintained during application and curing.
-- When applying at an ambient or substrate surface temperature below 5 °C, it is recommended to preheat the mixed paint to above 10 °C.
| Steel | Blast clean to Sa 2½ of international standard ISO 8501-1 or at least SP-6 of SSPC; the surface roughness after blasting is 40-70 µm. |
|---|---|
| Surfaces coated with a type-approved inorganic zinc silicate shop primer | Sweep blast to Sa 1 of international standard ISO 8501-1 (SPSS-SP7), or prepare to St 3 of international standard 8501-1 by power tool (SSPC-SP3). |
| Concrete | After the concrete is completely dry, with a moisture content below 4%, grind the surface flat and blow clean with high-pressure air. |
| Stainless steel | Degrease the surface with a grease cleaner or solvent, wash clean with clean water and dry. |
| Hot-sprayed zinc | Degrease and dewater the surface, then seal it with a thin spray. |
| FFD033IIA Abrasion-Resistant Epoxy | 26.2 kg/drum |
|---|---|
| FFD033IIB Abrasion-Resistant Epoxy Curing Agent | 3.8 kg/drum |
The product is for professional use only; it contains flammable substances, and site safety must comply with relevant national or local government regulations.
Avoid inhaling liquid, vapour or spray mist; do not allow skin and eyes to come into contact with the product; in confined and poorly ventilated spaces, increase ventilation. If accidentally splashed on the skin, wash immediately with a suitable cleaner, soap and water; if it enters the eyes, rinse thoroughly with water and seek medical attention immediately. For further details on safety and health and precautions for use, see the Material Safety Data Sheet (MSDS). In all circumstances, SKSHU shall be exempt from litigation liability for any indirect, special, incidental or consequential losses of any form arising from or caused by the use of this product
(whether for any omission, strict liability or tort).
The information in this data sheet is based entirely on our knowledge obtained in the laboratory and in practice. The use of coating products is usually outside our control, so the warranty is limited to the quality of the product itself. To comply with local regulations, the product may be adjusted
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.
The factory item codes of SKSHU FFD033II Abrasion-Resistant Epoxy are as follows.Item No.is the most accurate form when ordering;Colour/colour codecorresponds to the actual colour (RAL, GSB are colour chart codes);Packaging SpecificationsFactory complete-set specification format. Colors not listed may be ordered against the colour card.
| Item No. | Colour / colour code | Packaging Specifications |
|---|---|---|
| FFD033II | — | 30 KG |
This model has a total of1item numbers, all listed on this page; colours outside the table (including special colours and bulk packaging) can be confirmed by phone, delivery dates are advised according to the factory's current production schedule and stock. In the packaging specification, the "+" indicates the complete-set notation for two-component products (base + curing agent), subject to the factory specification; a "—" in the colour column denotes an auxiliary product, or that the item has no colour code in the factory system.