Product appearance: matt. Recommended dry film thickness: 200 µm. Colour: cream. Recommended wet film thickness: 310 µm. Composition: two-component. Theoretical spreading rate: for 200 µm dry film, approx. 3.2 m²/L. Mixing ratio (spreading rate varies with substrate roughness and permeability). Drying time: by volume base 50%, for 200 µm dry film. Parameters on this page: volume solids 63 ± 2%, dry film thickness 200 µm, theoretical spreading rate 6.4 m²/L/100 µm. Comparable models from the same brand: AMERCOAT 114 A epoxy filler 114 A, AMERCOAT 220 waterborne acrylic topcoat 220, AMERCOAT 240 SIGMACOVER 240 high-solids multipurpose epoxy 240.
Parameter source: PPG original technical data sheet (TDS) for PANTOXY RENDER Putty; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | — |
|---|---|
| Dry Film Thickness | — |
| Theoretical Spreading Rate | — |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | Water or Thinner No. 1. (1) If the product has dried, use Thinner No. 1 |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
Type/use: water-borne epoxy polyamide filler. Substrate: concrete.
Performance: indoor; outdoor. Used to fill pores, impregnated cracks and other defects on concrete surfaces before painting.
Approved by EDF (Electricité de France), CEMETE, CEA (French Atomic Energy Commission) and BINE; for on-site painting;
laboratories; maintenance;
Approved (by Nuclear Industry Second Institute) for use in nuclear power plants (passed radiation and LOCA combined tests, meets PIC system requirements). Applicable environments:
Complies with the PMUC specification for general aggressive environments.
Product appearance: matt. Recommended dry film thickness: 200 µm. Colour: cream. Recommended wet film thickness: 310 µm. Composition: two-component. Theoretical spreading rate: for 200 µm dry film, approx. 3.2 m²/L. Mixing ratio (spreading rate varies with substrate roughness and permeability). Drying time: by volume base 50%, for 200 µm dry film:
Curing agent: 50%. Dust-free: 2 h. Touch dry: 4 h. Thinner: water. Overcoatability: no induction period. Pantoxy Sealer Crevecoeur 130. Pot life: Saint Gobain EAP 2 h 30 min. Igadur Coatings* ambient temperature will affect the pot life and minimum recoating interval. Livolt 60. Density: recoating interval 1.70 ± 0.05, for 200 µm dry film:
Solids content: minimum* 24 h. Heat resistance: by volume 63% ± 2. All data related to the density and solids content of the topcoat are based on the product being white. These data are based on mixing of the appropriate products.
*See Overview.
Substrate and surface preparation; substrate type: concrete.
Ensure the surface is clean, dry and free from stains before painting.
Remove laitance and debris by a suitable method. Dust off.
Preparation of the product for use/thinning:
Stir the base mechanically and slowly add the curing agent until thoroughly mixed.
If necessary, thin the product according to the application conditions.
| Thinner: water | Cleaner: water or Thinner No. 1. (1) If the product has dried, use Thinner No. 1. |
|---|
Tool Thinner Nozzle pressure
| Brush, trowel, air spray gun | Not usable, usable, not usable | Not usable, 0/5% |
| High-pressure spray gun | Not available |
Application conditions:
Ambient temperature: +10 °C to +35 °C. Concrete moisture content shall not exceed 8%. Substrate temperature: at least 3 °C above the dew point. Note: good ventilation is required to facilitate moisture evaporation.
Two coats of filler are required:
The first coat removes air bubbles and levels the surface.
After the first coat dries, apply the second coat to smooth the surface.
When treating large defects, 30% quartz sand may be added to the first coat of putty.
Health and safety; flash point:
Base and hardener: none. Thinner No. 1: 21 °C < flash point < 55 °C. VOC content: 18 g/L, compliant with European paint and varnish sample criteria.
Packaging and storage: 20 L (base: 10 L / curing agent: 10 L). Storage: unopened, indoors between +5 °C and +35 °C, shelf life 12 months. Protect from freezing.
Sigma Coatings (China), Room 408, Baiteng Building, 318 Fuzhou Road, Shanghai 200001. Tel: 021-6391-2991; Fax: 021-6391-2700
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.