On primed surfaces: Shengbo, Weige EP 201 C, Yitielu putty, Pangdesi putty, Lifute 60. Use/dilution product preparation: mechanically stir the base, slowly add the hardener until completely mixed. Parameters on this page: number of components: two. Comparable products of the same brand: AMERCOAT 114 A Epoxy Filler 114 A, AMERCOAT 220 Water-borne Acrylic Topcoat 220, AMERCOAT 240 SIGMACOVER 240 High-solids Multi-purpose Epoxy 240.
Data source: PPG original Technical Data Sheet (TDS), "HYDRO PAINT Yitielu Coating"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | — |
|---|---|
| Dry Film Thickness | — |
| Theoretical Spreading Rate | — |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | Water or Thinner No. 1. (1) If the product has dried, use Thinner No. 1 |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
Performance: indoor; outdoor. Approved by EDF (Électricité de France), CEMETE (French nuclear energy laboratory), CEA (French nuclear energy centre) and BINE (Beijing Nuclear No. 2 Institute) for painting in nuclear workshops; on-site painting;
for power station use. (Radiation and LOCA requalification projects; maintenance;
(tested, meets PIC system) good effect on concrete surfaces. *1 Applicable environment:
Complies with the PMUC specification for general aggressive environments.
*1 French Highway and Bridges Authority characteristics (200C - relative humidity 65%). Product appearance; recommended dry film thickness: gloss 40 µm. Colour; recommended wet film thickness: see "Feida" colour chart 105 µm. Composition; theoretical spreading rate: two-component; for 40 µm dry film: 9.5 m²/L. Mixing ratio (spreading rate varies with substrate roughness and permeability). Drying time by volume, base: 64%; for 40 µm dry film:
Dust-free: 2 hours; hardener: 36%; touch dry: 7 hours; movable: 15 hours; thinner: water; recoatable; induction time: none; own activation period: Feida primer EP 3000 2 hours, Feida primer EP 1000. *Ambient temperature affects the activation period and minimum overcoating interval. Density; overcoating interval: 1.27 ± 0.05; for 40 µm dry film:
Solid content. Minimum*: 24 hours - maximum*: 1 year. Temperature resistance by volume*: 38%± 2; 120 °C (dry). All data relating to the density and solid content of the topcoat are based on the product being white. Also, these data are based on mixing appropriate products.
D8108-98 substrate type: concrete, cement surface or repaired dry suitable primed surface.
| On concrete or cement surfaces | Ensure the surface is clean, dry and free of stains. |
|---|
Remove laitance and debris by suitable methods. Dust. If substrate repair is needed, consult our technical service department.
On primed surfaces: Shengbo, Weige EP 201 C, Yitielu putty, Pangdesi putty, Lifute 60. Use/dilution product preparation:
Stir the base mechanically and slowly add the curing agent until thoroughly mixed.
If necessary, thin the product according to the application conditions.
| Thinner: water | Cleaner: water or Thinner No. 1. (1) If the product has dried, use Thinner No. 1. |
|---|
Tool Thinner Nozzle pressure
| Brush | Suitable | 0/5% | ||
| Roller | Suitable | 0/5% | ||
| Air spray gun | Suitable | 10/20% | 14 / 10e | 3 to 4 bar |
| High-pressure spray gun | Suitable | 5/10% | 15 to 19/1000e" | 205–256 bar |
When applying on concrete or cement surfaces, the first coat dilution rate should reach 20/25%.
Application conditions:
Ambient temperature: +10 °C to +35 °C. Concrete moisture content must not exceed 8%. Substrate temperature: at least +3 °C above the dew point. Note: good ventilation is required to facilitate moisture evaporation.
At humidity >60% and temperature <15 °C, the curing time is extended.
Health and safety; flash point:
Base and hardener: none. Thinner No. 1: 21 °C < flash point < 55 °C. Volatile organic content per litre: 40 g/L. This value complies with the European paint and varnish sample criteria.
Packaging and storage: 11 L (base: 7 L / hardener: 4 L). Storage: unopened indoors between +5 °C and +35 °C, can be stored for 12 months. Prevent freezing.
Shima Kalong Coating (China), Room 408, Baiteng Building, 318 Fuzhou Road, Shanghai - Postcode 200001. Tel: 021-6391-2991 Fax: 021-6391-2700. D8108-98
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.