Product appearance recommended dry film thickness: semi-gloss 50 to 70 µm. Colour recommended wet film thickness: light ochre yellow 90 to 130 µm. Composition theoretical spreading rate: two-component for 50 µm dry film: 10.8 m²/L. Mixing ratio for 70 µm dry film: 7.7 m²/L. Drying time by volume for 70 µm dry film. Parameters on this page: volume solids 54 ± 2%, dry film thickness 50–70 µm, theoretical spreading rate 5.4 m²/L/100 µm. Comparable products of the same brand: AMERCOAT 114 A Epoxy Filler 114 A, AMERCOAT 220 Water-borne Acrylic Topcoat 220, AMERCOAT 240 SIGMACOVER 240 High-solids Multi-purpose Epoxy 240.
Data source: PPG original Technical Data Sheet (TDS), "CENTREPOX N"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | — |
|---|---|
| Dry Film Thickness | — |
| Theoretical Spreading Rate | — |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | Thinner No. 1 application |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
Performance, indoor; outdoor;
Approved by EDF (Electricité de France), CEMETE (French Nuclear Energy Laboratory), CEA (French Nuclear Energy Commission) and BINE (Beijing Nuclear Engineering Research and Design Institute) for painting in nuclear workshops; on-site painting;
for power station use. (Radiation and LOCA requalification projects; maintenance;
combined experiments, meets PIC system) complies with ANSI N512, 101.2 specifications. Applicable environment:
Complies with PMUC specifications. Rural, urban, industrial and marine environments.
Product appearance recommended dry film thickness: semi-gloss 50 to 70 µm. Colour recommended wet film thickness: light ochre yellow 90 to 130 µm. Composition theoretical spreading rate: two-component for 50 µm dry film: 10.8 m²/L. Mixing ratio for 70 µm dry film: 7.7 m²/L. Drying time by volume for 70 µm dry film:
Base: 82%. Dust-free: 1 hour. Hardener: 18%. Touch dry: 1 hour 30 minutes. Handleable: 6 hours. Thinner: Thinner No. 1. Recoatable: none. Itself. Pot life: Shengfuge EAP − Feidagao ST 23. 28 hours. HYDRO RENDER coating*. Ambient temperature affects pot life and minimum overcoating interval. Weige EP / Weige PU. Density overcoating interval 1.45 ± 0.05 for 70 µm dry film:
Solids content minimum*: 6 hours - maximum*: 1 year. Service temperature by volume: 54% ± 2. Continuous 120 °C (dry). All data related to the density and solids content of the topcoat are based on the product being white. At the same time, these data are based on the mixing of the appropriate products.
*See Overview.
CHALLENGING TIMED 4008-98
Substrate and surface preparation. Substrate type: steel surface.
Blast clean to Sa 2½ per ISO 8501-1.
Use/thinning
Stir the base mechanically and slowly add the curing agent until thoroughly mixed.
If necessary, thin the product according to the application conditions.
| Thinner: Thinner No. 1 | Cleaning agent: Thinner No. 1 application |
|---|---|
| Tools | Thinning, nozzle pressure |
| Brush | Suitable | Ready for use | (for small areas only) | |
| Roller | Suitable | 10/20% | ||
| Air spray gun | Suitable | 10/20% | 14 to 10e | 3 to 4 bar |
| High-pressure spray gun | Suitable | 5/15% | 17 to 21/1000e" | 205–256 bar |
| Application conditions | Ambient temperature: +5 °C to +35 °C |
|---|
Health and safety
| Flash Point | Base and hardener: 21 °C < flash point < 55 °C |
|---|
This figure complies with European paint and varnish sample criteria.
Packaging and storage. Packaging: 20 L (base: 16.4 L / hardener: 3.6 L). Storage: unopened indoors between +5 °C and +35 °C, can be stored for 12 months.
Sigma Coatings (China), Room 408, Baiteng Building, 318 Fuzhou Road, Shanghai 200001. Tel: 021-6391-2991; Fax: 021-6391-2700
08-98
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.