ZIES213 Inorganic Zinc-Rich Primer is a zinc-rich primer. It can be used with most paint systems as a high-performance anticorrosive coating for various steel structures. High-performance, grey, to be used with ZIES218 zinc powder hardener. Parameters on this page: dry film thickness 75 µm, theoretical spreading rate 3.77 m²/kg.
Parameter source: OSAKA original technical data sheet (TDS) for ZIES213 Inorganic Zinc-Rich Primer; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 65% |
|---|---|
| Dry Film Thickness | 75 µm |
| Theoretical Spreading Rate | 3.77 m²/kg |
| VOC | 301 g/L |
| Density / Specific Gravity | Approx. 2.80 kg/L |
| Number of Components | Two-component |
| Thinner | OUP 107 |
| Mixing Ratio | ZIES213 : ZIES218 = 4 : 1 |
| Pot Life | 23 °C: 4 h |
High-performance, grey, to be used with ZIES218 zinc powder hardener.
The film has a high zinc powder content (more than 80% zinc powder by weight in the dry film), providing good cathodic protection, excellent abrasion resistance, impact resistance, anticorrosive properties and durability; fast drying, low-temperature curing, excellent solvent resistance and heat resistance up to 500 °C. It can be used with most paint systems as a high-performance anticorrosive coating for various steel structures.
| Volume Solids | 65% |
|---|---|
| Dry Film Thickness | 75 µm |
| Theoretical Spreading Rate | 3.77 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 301 g/L |
| Mixing Ratio | ZIES213 : ZIES218 = 4 : 1 |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable, but not recommended. |
| Thinner | OUP 107 |
| Paint equipment cleaner | OUP 107 |
| Pot life | 23 °C: 4 h |
| Drying Time | ||||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 23°C | 15 | 8 | 8 h | 14 days |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 30 kg in a 20 L container |
| Flash Point | Above 13 °C (mixture) |
| density | Approx. 2.80 kg/L |
Steel surfaces: blast clean to Sa 2.5 of ISO 8501:2007 or prepare to St 3 by hand or power tool. Keep clean and dry.
The minimum recoating interval depends on the relative humidity; the maximum recoating interval depends on climatic and environmental conditions. Surfaces coated with this product must be clean, dry and free from zinc salts before recoating. Overcoating with alkyd paint is not recommended.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.