WPF1001 One-component Water-borne Surface-tolerant Coating belongs to Water-borne. For the corrosion protection of steel structure surfaces under low to medium C2–C4 atmospheric corrosion environments, widely used in automotive chassis, fans, mining machinery, power equipment and construction machinery and other fields. A one-component water-borne surface-tolerant coating with extremely low VOC, safe and environmentally friendly, with good adhesion to metal substrates, good rust-preventive performance and weather resistance. Parameters on this page: dry film thickness 30–60 µm, theoretical spreading rate 9.35 m²/kg, number of components one-component.
Parameter source: OSAKA original technical data sheet (TDS) “WPF1001 One-component Water-borne Surface-tolerant Coating”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 43% |
|---|---|
| Dry Film Thickness | 30–60 µm |
| Theoretical Spreading Rate | 9.35 m²/kg |
| VOC | — |
| Density / Specific Gravity | 1.15 kg/L |
| Number of Components | One-component |
| Thinner | Clean fresh water |
| Mixing Ratio | Single pack |
| Colour / Appearance | White, black or other colours specified by the customer |
A one-component water-borne surface-tolerant coating with extremely low VOC, safe and environmentally friendly, with good adhesion to metal substrates, good rust-preventive performance and weather resistance. Capable of air drying at ambient temperature or low-temperature baking.
For corrosion protection of steel structures in low to medium atmospheric corrosion environments C2–C4, widely used for automotive chassis, fans, mining machinery, power equipment and construction machinery.
| Colour | White, black or other colours specified by the customer |
|---|---|
| Volume Solids | 43% |
| Typical dry film thickness | 30–60 µm |
| Theoretical Spreading Rate | 9.35 m²/kg (dry film thickness calculated at 40 µm) |
| Practical Spreading Rate | Allowing a suitable loss |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; output pressure 12–15 MPa |
| Conventional spray | Recommended: nozzle size 1.3–1.5 mm; output pressure 0.3–0.4 MPa |
| Brush | Recommended for touch-up or small-area application. Take care to achieve the specified dry film thickness. |
| Roller application | Recommended for small-area application. Take care to achieve the specified dry film thickness. |
| Thinner | Clean fresh water |
| Paint equipment cleaner | Clean fresh water |
| Pot life | Unlimited |
| Drying Time | |||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Minimum recoat interval (h) |
| 23°C | 1 | 12 | |
Note: ventilation, temperature, relative humidity and film thickness all affect drying and curing times. The data above are measured under well-ventilated conditions with relative humidity <75%.
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| density | 1.15 kg/L |
Abrasive blast cleaning to Sa2.5 of ISO 8501:2007, or hand or power tool cleaning to St3. The workpiece surface shall be kept clean, dry and free from contamination; substrate temperature shall be at least 3 °C above dew point.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.