TR627 High-temperature Coating 800 °C is a high-temperature paint. Used for protective decoration of various mechanical equipment surfaces at temperatures up to 800 °C. An organic-inorganic composite high-temperature coating, limited colours. Parameters on this page: dry film thickness 20–60 µm, theoretical spreading rate 9.2 m²/kg.
Data source: OSAKA original Technical Data Sheet (TDS), "TR627 High-temperature Coating 800 °C"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60% |
|---|---|
| Dry Film Thickness | 20–60 µm |
| Theoretical Spreading Rate | 9.2 m²/kg |
| VOC | 344 g/L |
| Density / Specific Gravity | Approx. 1.3 kg/L |
| Number of Components | One-component |
| Thinner | OUP 102, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
| Pot Life | Unlimited |
An organic-inorganic composite high-temperature coating, limited colours.
Used for protective decoration of various mechanical equipment surfaces at temperatures up to 800 °C.
| Volume Solids | 60% |
|---|---|
| Dry Film Thickness | 20–60 µm |
| Theoretical Spreading Rate | 9.2 m²/kg, based on the stated volume solids and 50 µm dry film thickness |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 344 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: tip size 0.43–0.53 mm; fluid pressure ≥ 17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable, but not recommended. |
| Thinner | OUP 102, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP102 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 23°C | 30 | 36 | 36 h | Unlimited |
| 35°C | 20 | 24 | 24 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| Flash Point | Above 35 °C |
| density | Approx. 1.3 kg/L |
Steel surfaces: blast clean to Sa2.5 of ISO 8501:2007, or clean by hand or power tool to St3. Keep clean and dry. Stir thoroughly until uniform before use.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.