TR603-1/TR603-2 Silicone Heat-Resistant Aluminium Paint 600 °C / Silicone Heat-Resistant Aluminium Paint 600 °C is a heat-resistant coating, in the silicone coating system. Used for surface protection and decoration of various machinery and equipment at temperatures up to 600 °C, such as engines, boilers and pipeline surfaces. One-component or two-component silicone resin paint. Parameters on this page: dry film thickness 30-60 µm, theoretical spreading rate 10 m²/kg, number of components: two-component.
Parameter source: OSAKA original technical data sheet (TDS) for TR603-1/TR603-2 Silicone Heat-Resistant Aluminium Paint 600 °C (one-component)/Silicone Heat-Resistant Aluminium Paint 600 °C (two-component); spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 43% |
|---|---|
| Dry Film Thickness | 30–60 µm |
| Theoretical Spreading Rate | 10 m²/kg |
| VOC | 491 g/L |
| Density / Specific Gravity | Approx. 1.07 kg/L |
| Number of Components | Two-component |
| Thinner | OUP 102, recommended addition 3%–5% |
| Mixing Ratio | TR603-1: single can; TR603-2: Component A : Component B = 4:1 (by weight) |
| Colour / Appearance | Silver grey |
Single-can or two-can silicone resin coating.
For protective and decorative coating of various mechanical equipment surfaces at temperatures up to 600 °C, such as engines, boilers and pipelines.
| Colour | Silver grey |
|---|---|
| Volume Solids | 43% |
| Dry Film Thickness | 30–60 µm |
| Theoretical Spreading Rate | 10 m²/kg, at 40 µm dry film thickness. |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 491 g/L |
| Mixing Ratio | TR603-1: single can; TR603-2: Component A : Component B = 4:1 (by weight) |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Applicable |
| Conventional spray | Suitable, but not recommended. |
| Thinner | OUP 102, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 102 |
| Pot life | TR603-1: unlimited; TR603-2: 23 °C: 4 h |
| Drying Time | |||
| Substrate Temperature | Touch dry (min) | TR603-2 | TR603-1 |
| Hard dry (h) | Hard dry | ||
| 23°C | 30 | 6 | Force dry at 180–200 °C for 30–60 min |
| 35°C | 15 | 3 | |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | TR603-1: 20 kg in a 20 L drum; TR603-2: Component A: 20 kg in a 20 L drum; Component B: 5 kg in a 5 L drum |
| Flash Point | Above 23 °C |
| density | Approx. 1.07 kg/L |
Before use alone, all surfaces to be coated must be assessed and treated in accordance with ISO standards; if grease is present, clean with solvent to SSPC-SP1; blast clean to Sa 2.5 or power tool clean to St 3; remove dust and contaminants. With a suitable heat-resistant primer, keep the primer surface clean and dry.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.