SPE902-M Vinyl Ester Resin Glass Flake Coating is a glass flake coating in the vinyl ester system. Suitable for internal-wall corrosion protection of low-temperature flue gas desulphurization systems, and can be used as an intermediate coat for all concrete anticorrosive work, including flue ducts, tank interiors, drainage pits, channels and slurry pools. A three-component product composed of bisphenol-A vinyl ester resin, coarse glass flake of 20–80 mesh, other pigments/fillers, a small amount of reactive diluent and additives; mix evenly in the specified ratio before application. Parameters on this page: dry film thickness 800–1000 µm; theoretical spreading rate 0.70 m²/kg; number of components: three.
Source: OSAKA original technical data sheet (TDS) 'SPE902-M Vinyl Ester Resin Glass Flake Coating'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 96% |
|---|---|
| Dry Film Thickness | 800–1000 µm |
| Theoretical Spreading Rate | 0.70 m²/kg |
| VOC | <40 g/L |
| Density / Specific Gravity | 1.40 kg/L |
| Number of Components | Three-component |
| Thinner | OUP 115, not required |
| Mixing Ratio | Component A : Component B : Component C = 20 : 0.3 : 0.2 (by weight) |
| Colour / Appearance | White, light green or other colours as specified by the customer |
A three-component product composed of bisphenol-A vinyl ester resin, coarse glass flake of 20–80 mesh, other pigments/fillers, a small amount of reactive diluent and additives; mix evenly in the specified ratio before application. - High abrasion resistance and hardness. - Good thermal cycling resistance, fatigue resistance and adhesion. - Labyrinth effect with strong resistance to medium permeation. - High chemical resistance
Suitable for internal-wall corrosion protection of low-temperature flue gas desulphurization systems, and can be used as an intermediate coat for all concrete anticorrosive work, including flue ducts, tank interiors, drainage pits, channels and slurry pools. Also suitable for areas in contact with other chemical media.
| Colour | White, light green or other colours as specified by the customer |
|---|---|
| Volume Solids | 96% |
| Dry Film Thickness | 800–1000 µm |
| Theoretical Spreading Rate | 0.70 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | <40 g/L |
| Mixing Ratio | Component A : Component B : Component C = 20 : 0.3 : 0.2 (by weight) |
|---|---|
| Induction Time | No induction required |
| Squeegee application | Recommended |
| Thinner | OUP 115, not required |
| Paint equipment cleaner | OUP 115 |
| Pot life | 15 °C: 60 min; 23 °C: 35 min; 35 °C: 15 min |
| Drying Time | |||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Fully cured | Recoat Interval | |
| Minimum | Maximum | ||||
| 15°C | 8 | 8 days | 8 h | 36 h | |
| 23°C | 4 | 4 days | 4 h | 24 h | |
| 35°C | 2 | 2 days | 2 h | 12 h | |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 20 kg in a 20 L container; Component B: 0.3 kg in a 300 mL plastic bottle; Component C: 0.2 kg in a 300 mL plastic bottle |
| Flash Point | Above 32 °C |
| density | 1.40 kg/L |
Primed surfaces shall be kept clean and dry.
Application conditions: ambient temperature 5–40 °C, substrate temperature at least 3 °C above the dew point, and good ventilation at the application site.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.