SFCP1101 Fluorocarbon Coating is a fluorocarbon paint used as a topcoat. It is suitable for long-term corrosion protection of steel structures in extremely severe atmospheric corrosive environments, with excellent gloss and colour retention, excellent weathering resistance, a surface water contact angle of 80–100°, stain resistance and easy cleaning. High gloss or matt, various colours, two-component fluorocarbon topcoat with an aliphatic isocyanate hardener as Component B. Parameters on this page: dry film thickness 50–70 µm, theoretical spreading rate 9.1–10.5 m²/kg, number of components two-component.
Parameter source: OSAKA manufacturer's Technical Data Sheet (TDS) "SFCP1101 Fluorocarbon Coating (Topcoat)"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 55% |
|---|---|
| Dry Film Thickness | 50–70 µm |
| Theoretical Spreading Rate | 9.1–10.5 m²/kg |
| VOC | 387 g/L |
| Density / Specific Gravity | 1.05–1.20 kg/L |
| Number of Components | Two-component |
| Thinner | OUP 112, recommended addition 3%–5% |
| Mixing Ratio | Component A : Component B = 9:1 (by weight) |
| Colour / Appearance | Various colours |
High gloss or matt, various colours, two-component fluorocarbon topcoat with an aliphatic isocyanate hardener as Component B.
Suitable for long-term corrosion protection of steel structures in extremely severe atmospheric corrosive environments, with excellent gloss and colour retention, excellent weathering resistance, a surface water contact angle of 80–100°, stain resistance and easy cleaning.
| Colour | Various colours |
|---|---|
| Volume Solids | 55% |
| Dry Film Thickness | 50–70 µm |
| Theoretical Spreading Rate | 9.1–10.5 m²/kg, based on 50 µm dry film thickness. |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 387 g/L |
| Mixing Ratio | Component A : Component B = 9:1 (by weight) |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.49 mm; fluid pressure ≥15.5 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable, but not recommended. |
| Thinner | OUP 112, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 112 |
| Pot life | 23 °C: 4 h |
| Drying Time | ||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 2 | 30 | 24 h | 5 days |
| 23°C | 1 | 16 | 12 h | 3 days |
| 35°C | 0.5 | 8 | 4 h | 1 day |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 18 kg in a 20 L container; Component B: 2 kg in a 4 L container |
| Flash Point | Above 23 °C |
| density | 1.05–1.20 kg/L |
Steel structures: for surfaces already primed or intermediate-coated, which must be kept clean, dry and free from oil. Building exterior walls: new concrete or cement mortar walls completed at least 10 days previously, with a moisture content below 10%; the wall surface must be flat and sound, levelled with a suitable putty, sanded and then coated with this product.
Mix in the specified ratio and use immediately; use up within the pot life. Avoid contact with moisture during storage and application. At high temperatures, the maximum recoat interval is limited to one day.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.