HCP142 High Chlorinated Polyethylene Primer belongs to primers. Suitable for corrosion protection of steel structures exposed to industrial atmosphere, chemically polluted atmosphere and acid, alkali and salt corrosive environments, and for corrosion protection of concrete equipment surfaces. The film offers excellent water resistance, moisture resistance and chemical resistance, good adhesion, rapid drying and easy application. One-component, grey or iron red. Parameters on this page: DFT 35 µm equivalent to 100 µm WFT, theoretical spreading rate 8 m²/kg, number of components one-component.
Parameter source: OSAKA original technical data sheet (TDS) for HCP142 High Chlorinated Polyethylene Primer; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 35% |
|---|---|
| Dry Film Thickness | 35 µm corresponds to 100 µm WFT |
| Theoretical Spreading Rate | 8 m²/kg |
| VOC | 559 g/L |
| Density / Specific Gravity | Approx. 1.25 kg/L |
| Number of Components | One-component |
| Flash Point | 38°C |
| Thinner | OUP 101, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
One-component, grey or iron red
Suitable for corrosion protection of steel structures exposed to industrial atmospheres, chemically polluted atmospheres and acid, alkali and salt corrosive environments, and also for concrete equipment surfaces. The film has high water resistance, moisture resistance and chemical resistance, good adhesion, fast drying and easy application.
| Volume Solids | 35% |
|---|---|
| Dry Film Thickness | 35 µm corresponds to 100 µm WFT |
| Theoretical Spreading Rate | 8 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 559 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable, but not recommended. |
| Thinner | OUP 101, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 101 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 60 | 16 | 16 h | Unlimited |
| 23°C | 30 | 8 | 8 h | Unlimited |
| 35°C | 15 | 4 | 4 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 25 kg in a 20 L container |
| Flash Point | 38°C |
| density | Approx. 1.25 kg/L |
Steel surface: blast cleaning to Sa2.5 of ISO 8501:2007, or hand or power tool cleaning to St3. Keep clean and dry. Concrete surface: remove oil, grease, dust and other contaminants from the surface.
Subsequent coat: various high chlorinated polyethylene functional coatings (topcoat)
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.