F01-15 Phenolic Varnish belongs to phenolic coatings and is used as a topcoat. Suitable for clear finishing of interior and exterior metal and wood surfaces; also applicable to furniture coating. Single-component, transparent, formulated from phenolic resin, drier and solvent naphtha; the coating provides good adhesion and water resistance, high gloss and full film, and dries at room temperature. Parameters on this page: DFT 20 µm, theoretical spreading rate 16.67 m²/kg, number of components single-component.
Parameter source: OSAKA original technical data sheet (TDS) for F01-15 Phenolic Varnish; values such as spreading rate are converted from TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 35% |
|---|---|
| Dry Film Thickness | 20 µm |
| Theoretical Spreading Rate | 16.67 m²/kg |
| VOC | 563 g/L |
| Density / Specific Gravity | Approx. 1.05 kg/L |
| Number of Components | One-component |
| Flash Point | 35°C |
| Thinner | OUP 100, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
Single-component, transparent, formulated from phenolic resin, drier and solvent naphtha; the coating provides good adhesion and water resistance, high gloss and full film, and dries at room temperature.
Suitable for clear finishing of interior and exterior metal and wood surfaces; also applicable to furniture coating.
| Volume Solids | 35% |
|---|---|
| Dry Film Thickness | 20 µm corresponds to 57 µm WFT |
| Theoretical Spreading Rate | Approx. 16.67 m²/kg at 20 µm DFT |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 563 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle orifice 0.43–0.53 mm; fluid pressure: ≥15.5 MPa |
| Brush or roller | Recommended |
| Conventional spray | Recommended |
| Thinner | OUP 100, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 100 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 4 | 48 | 48 h | 7 days |
| 23°C | 2 | 24 | 24 h | 7 days |
| 35°C | 1 | 16 | 16 h | 7 days |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| Flash Point | 35°C |
| density | Approx. 1.05 kg/L |
Varnish is generally applied over the topcoat; the topcoated surface shall be kept clean and dry.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.