EPSP409 Solvent-free Epoxy Static-conductive Oil Tank Coating belongs to Epoxy. Suitable for internal lining of various oil storage equipment or oil pipelines. Due to solvent-free, also suitable for application in poorly ventilated environments. The film has excellent oil resistance, no contamination to various oils, easy to clean, strong adhesion, static-conductive, can avoid fire or explosion caused by static electricity. Parameters on this page: volume solids 100%, theoretical spreading rate 2.4–3.6 m²/kg, number of components two-component.
Parameter source: OSAKA original technical data sheet (TDS) 'EPSP409 Solvent-free Epoxy Static-conductive Oil Tank Coating'; values such as spreading rate are converted from TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 100% |
|---|---|
| Dry Film Thickness | 200 µm |
| Theoretical Spreading Rate | 2.4–3.6 m²/kg |
| VOC | 6 g/L |
| Density / Specific Gravity | 1.4 kg/L |
| Number of Components | Two-component |
| Flash Point | >65 °C (mixture, Component A, Component B) |
| Thinner | Not required |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
Two-component, solvent-free, room temperature curing. The film has excellent oil resistance, no contamination to various oils, easy to clean, strong adhesion, static-conductive, can avoid fire or explosion caused by static electricity.
Suitable for internal lining of various oil storage equipment or oil pipelines. Due to solvent-free, also suitable for application in poorly ventilated environments.
| Colour | Black, grey, etc. |
|---|---|
| Volume Solids | 100% |
| Dry Film Thickness | Recommended: 200 µm |
| Theoretical Spreading Rate | 2.4–3.6 m²/kg |
| Static-conductive resistance | 10^8–10^11 ohm |
| Volatile organic compound content | 6 g/L |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
|---|---|
| Airless spray | Recommended, use high-power spray pump |
| Brush or roller | Can be used |
| Air spray | N/A |
| Thinner | Not required |
| Paint equipment cleaner | OUP 103 |
| Pot life | Summer type: 35 °C: 20–25 min; 23 °C: 30–45 min. Winter type: 15 °C: 30–45 min; 5 °C: 45–60 min |
| Drying Time | |||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Full cure time (days) |
| 5°C | 8 | 24 | 10 |
| 15°C | 6 | 12 | 7 |
| 23°C | 6 | 12 | 7 |
| 35°C | 4 | 8 | 3 |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 16 kg in a 20 L drum; Component B: 4 kg in a 4 L drum |
| Flash Point | >65 °C (mixture, Component A, Component B) |
| density | 1.4 kg/L |
Surfaces without primer must be blast cleaned or sand blasted to Sa2.5, and kept clean. When the application ambient temperature is 20 °C or above, summer type is recommended; at 0–20 °C, use winter type, but below 5 °C, the coating cures slowly. For this product, mix immediately before use, mix only the amount needed, stir thoroughly, and use within the pot life to avoid gelation and waste. After application of this product, appropriate heating (45–120 °C) can shorten drying time and improve film properties. When the temperature is below 15 °C, the paint should be appropriately heated during spraying. Note: pot life will be shortened. After application of this coating, it must be fully cured before being put into service.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.