EPSP403 Solvent-free Epoxy Phenolic Coating is an epoxy paint. Suitable for application in poorly ventilated environments, such as oil storage tanks, ship oil and water tanks, concrete storage tanks, chemical storage tanks and solvent storage tanks etc. The coating has excellent chemical corrosion resistance, oil resistance, water resistance, seawater resistance, heat resistance and solvent resistance. Parameters on this page: volume solids 100%, theoretical spreading rate 3.9 m²/kg, number of components: two.
Data source: OSAKA original Technical Data Sheet (TDS), "EPSP403 Solvent-free Epoxy Phenolic Coating"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 100% |
|---|---|
| Dry Film Thickness | 200 µm, adjusted according to different use requirements |
| Theoretical Spreading Rate | 3.9 m2/Kg |
| VOC | 9 g/L |
| Density / Specific Gravity | 1.3 kg/L |
| Number of Components | Two-component |
| Flash Point | >65 °C (mixture, Component A, Component B) |
| Thinner | Not required |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
A two-component solvent-free coating, curable at room temperature. Strong film adhesion, excellent mechanical properties, easy application. The coating has excellent chemical corrosion resistance, oil resistance, water resistance, seawater resistance, heat resistance and solvent resistance.
Suitable for application in poorly ventilated environments, such as oil storage tanks, ship oil and water tanks, concrete storage tanks, chemical storage tanks and solvent storage tanks etc.
| Colour | Grey, iron red etc. |
|---|---|
| Volume Solids | 100% |
| Dry Film Thickness | Recommended: 200 µm, adjusted according to different use requirements |
| Theoretical Spreading Rate | Based on 200 µm dry film thickness, 3.9 m²/kg. |
| Volatile organic compound content | 9 g/L |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
|---|---|
| Squeegee application | Suitable for small-area application or touch-up |
| Airless spray | May be used, for smooth surfaces only. |
| Brush or roller | May be used, for smooth surfaces only. |
| Air spray | N/A |
| Thinner | Not required |
| Paint equipment cleaner | OUP 103 |
| Pot life | 60 minutes at 23 °C |
| Drying Time | |||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Full cure time (days) |
| 23°C | 16 | 48 | 7 |
| 35°C | 10 | 24 | 7 |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 16 kg in a 20 L drum; Component B: 4 kg in a 4 L drum |
| Flash Point | >65 °C (mixture, Component A, Component B) |
| density | 1.3 kg/L |
Unprimed surfaces shall be shot-blasted or blasted to Sa2.5. Compatible with various shop primers and anticorrosive coatings. Mix only the amount needed and use within the pot life, stirring thoroughly, to avoid waste from gelling. After coating, soak with clean water for one week and rinse three times, then it may store potable water and foodstuffs. After coating, moderate heating (45–120 °C) shortens the drying time and improves film performance. Below 15 °C, heat the paint appropriately when spraying, noting that the pot life shortens. The film appearance depends on ambient temperature and humidity; a good appearance is obtained above 10 °C and below 85% relative humidity.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.