EPSP401 Solvent-free Epoxy Anticorrosive Coating is an epoxy coating. Suitable for application in poorly ventilated environments such as oil storage tanks and oil/water tanks. The film provides good chemical resistance, oil resistance, seawater resistance and heat resistance, good adhesion and mechanical properties, and is easy to apply. Parameters on this page: volume solids 100%, dry film thickness approx. 0.2–0.3 mm, theoretical spreading rate 3.33–3.57 m²/kg.
Parameter source: OSAKA manufacturer's Technical Data Sheet (TDS) "EPSP401 Solvent-free Epoxy Anticorrosive Coating"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 100% |
|---|---|
| Dry Film Thickness | Approx. 0.2–0.3 mm |
| Theoretical Spreading Rate | 3.33-3.57 m2/Kg |
| VOC | 9 g/L |
| Density / Specific Gravity | 1.4–1.5 kg/L |
| Number of Components | Two-component |
| Flash Point | >65 °C (mixture, Component A, Component B) |
| Thinner | Not required |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
Two-component, room-temperature curing; solvent-free, odourless and non-polluting film. The film provides good chemical resistance, oil resistance, seawater resistance and heat resistance, good adhesion and mechanical properties, and is easy to apply.
Suitable for application in poorly ventilated environments such as oil storage tanks and oil/water tanks.
| Colour | White, grey and other colours |
|---|---|
| Volume Solids | 100% |
| Dry Film Thickness | Approx. 0.2–0.3 mm |
| Theoretical Spreading Rate | 3.33–3.57 m²/kg based on 200 µm dry film thickness. |
| Volatile organic compound content | 9 g/L |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
|---|---|
| Airless spray | May be used, for smooth surfaces only. |
| Brush or roller | May be used, for smooth surfaces only. |
| Air spray | N/A |
| Thinner | Not required |
| Paint equipment cleaner | OUP 103 |
| Pot life | 23°C: 60 min; 35°C: 45 min |
| Drying Time | |||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Full cure time (days) |
| 23°C | 6 | 24 | 7 |
| 35°C | 4 | 16 | 7 |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 16 kg in a 20 L drum; Component B: 4 kg in a 4 L drum |
| Flash Point | >65 °C (mixture, Component A, Component B) |
| density | 1.4–1.5 kg/L |
Surfaces without primer shall be prepared by shot blasting or abrasive blast cleaning to Sa2.5. Compatible with various shop primers and anticorrosive primers. Mix the product immediately before use in the quantity required, stir thoroughly and use within the pot life to avoid gelling and waste. After application, moderate heating (45–120°C) shortens drying time and improves film properties. Film appearance depends on ambient temperature and humidity; good appearance is obtained at ambient temperature above 10°C and relative humidity below 85%.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.