EPSP394 Epoxy Phenolic Oil Tank Coating is an epoxy coating. Used for anticorrosive and antistatic coating of the interior walls of tanks and compartments carrying crude oil, gasoline, kerosene, diesel and naphtha. Light grey, using a metal oxide composite static-dissipative medium. Parameters on this page: dry film thickness 125 µm, theoretical spreading rate 4.28 m²/kg, number of components: two-component.
Parameter source: OSAKA original technical data sheet (TDS) for EPSP394 Epoxy Phenolic Oil Tank Coating; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 75% |
|---|---|
| Dry Film Thickness | 125 µm |
| Theoretical Spreading Rate | 4.28 m²/kg |
| VOC | 215 g/L |
| Density / Specific Gravity | 1.40 kg/L |
| Number of Components | Two-component |
| Flash Point | 22°C |
| Thinner | OUP 103, recommended addition 3%–5% |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
Light grey, using a metal-oxide composite static-dissipative medium.
Used for anticorrosive and antistatic coating of the interior walls of tanks and compartments carrying crude oil, gasoline, kerosene, diesel and naphtha. It has excellent oil resistance, corrosion resistance and good static-dissipative properties.
| Volume Solids | 75% |
|---|---|
| Dry Film Thickness | 125 µm |
| Theoretical Spreading Rate | 4.28 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 215 g/L |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
|---|---|
| Airless spray | Recommended: tip size 0.53–0.68 mm; fluid pressure ≥ 21.1 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable but not recommended. |
| Thinner | OUP 103, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 103 |
| Pot life | 23 °C — 3 h |
| Drying Time | ||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 4 | 36 | 36 h | 7 days |
| 23°C | 2 | 24 | 24 h | 7 days |
| 35°C | 0.5 | 18 | 18 h | 7 days |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 16 kg in a 20 L container; Component B: 4 kg in a 4 L container |
| Flash Point | 22°C |
| density | 1.40 kg/L |
Steel surfaces: abrasive blast clean to Sa 2.5 (ISO 8501:2007) or clean by hand/power tools to St 3.
Recommended number of coats: two coats by airless spray, to a dry film thickness of 250 µm. Previous coat: inorganic zinc-rich primer, epoxy zinc-rich primer, etc.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.