CR102 Chlorinated Rubber Intermediate/Topcoat belongs to chlorinated rubber coatings and is used as an intermediate coat. For corrosion protection of steel structures and concrete exposed to moderate atmospheric corrosive environments; excellent water and chemical resistance. Single-component, silver or other colours, fast drying, applicable at low temperatures. Parameters on this page: dry film thickness 50 µm equivalent to 111 µm wet film, theoretical spreading rate 7.5 m²/kg, number of components single-component.
Parameter source: OSAKA original technical data sheet (TDS) "CR102 Chlorinated Rubber Intermediate/Topcoat"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 45% |
|---|---|
| Dry Film Thickness | 50 µm corresponds to 111 µm WFT |
| Theoretical Spreading Rate | 7.5 m²/kg |
| VOC | 473 g/L |
| Density / Specific Gravity | Approx. 1.2 kg/L |
| Number of Components | One-component |
| Thinner | OUP 100, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
| Pot Life | Unlimited |
Single-component, silver or other colours, fast drying, applicable at low temperatures.
For corrosion protection of steel and concrete exposed to medium atmospheric corrosion, with high water and chemical resistance.
| Volume Solids | 45% |
|---|---|
| Dry Film Thickness | 50 µm corresponds to 111 µm WFT |
| Theoretical Spreading Rate | 7.5 m²/kg, based on the specified volume solids and 50 µm dry film thickness |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 473 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable but not recommended. |
| Thinner | OUP 100, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 100 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 40 | 16 | 16 h | Unlimited |
| 23°C | 20 | 5 | 5 h | Unlimited |
| 35°C | 10 | 2 | 2 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| Flash Point | Above 23 °C |
| density | Approx. 1.2 kg/L |
Steel surfaces: abrasive blast clean to Sa 2.5 (ISO 8501:2007) or clean by hand or power tools to St 3. Keep clean and dry.
Not resistant to solvents, oils and fats; thermoplastic. Softens and decomposes readily above 80°C.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.