CP164 Chlorosulfonated Polyethylene Primer belongs to primers. Widely used in petrochemical, power, bridge, pipeline and machinery fields, and for the protection of equipment in water conservancy projects, reservoirs, cooling towers, wastewater tanks, ports and docks; provides excellent resistance to chemical and electrochemical corrosion and good abrasion resistance and cold resistance. One-component, iron red or grey, solvent-borne self-drying type. Parameters on this page: dry film thickness 30 µm equivalent to 85 µm wet film, theoretical spreading rate 9.48 m²/kg, number of components one-component.
Source of parameters: OSAKA original technical data sheet (TDS) "CP164 Chlorosulfonated Polyethylene Primer"; spreading rate and other values are converted from TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 35% |
|---|---|
| Dry Film Thickness | 30 µm DFT corresponds to 85 µm WFT |
| Theoretical Spreading Rate | 9.48 m²/kg |
| VOC | 560 g/L |
| Density / Specific Gravity | Approx. 1.23 kg/L |
| Number of Components | One-component |
| Flash Point | 37°C |
| Thinner | OUP 111, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
One-component, iron red or grey, solvent-borne self-drying type
Widely used in petrochemical, power, bridge, pipeline and machinery fields, and for the protection of equipment in water conservancy projects, reservoirs, cooling towers, wastewater tanks, ports and docks; provides excellent resistance to chemical and electrochemical corrosion and good abrasion resistance and cold resistance.
| Volume Solids | 35% |
|---|---|
| Dry Film Thickness | 30 µm DFT corresponds to 85 µm WFT |
| Theoretical Spreading Rate | 9.48 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 560 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable but not recommended. |
| Thinner | OUP 111, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 111 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 60 | 16 | 16 h | Unlimited |
| 23°C | 30 | 8 | 8 h | Unlimited |
| 35°C | 15 | 4 | 4 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| Flash Point | 37°C |
| density | Approx. 1.23 kg/L |
Steel surface: abrasive blast cleaning to Sa2.5 of ISO 8501:2007, or hand or power tool cleaning to St3; the surface shall be clean and dry.
Subsequent coat: various chlorosulfonated polyethylene functional coatings (topcoat)
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.