AL067 Waterborne Alkyd Enamel is a waterborne coating used as a topcoat. For fans, axles, automotive chassis, guardrails, hardware and other light-industry metal products. A one-component waterborne air-drying industrial protective topcoat; the film-forming mechanism is oxidative drying and curing, and strong ventilation helps accelerate film cure. Water is the dispersion medium, offering safety, environmental protection and flame retardancy, with excellent adhesion to steel substrates and good corrosion resistance. Parameters on this page: dry film thickness 40 µm, theoretical spreading rate 8.83 m²/kg, number of components one.
Source: OSAKA original technical data sheet (TDS) "AL067 Waterborne Alkyd Enamel"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 41% |
|---|---|
| Dry Film Thickness | 40 µm |
| Theoretical Spreading Rate | 8.83 m²/kg |
| VOC | — |
| Density / Specific Gravity | 1.16 kg/L |
| Number of Components | One-component |
| Thinner | Clean fresh water |
| Mixing Ratio | Single pack |
| Colour / Appearance | White, or other colours as specified by the customer |
A one-component waterborne air-drying industrial protective topcoat; the film-forming mechanism is oxidative drying and curing, and strong ventilation helps accelerate film cure. Water is the dispersion medium, offering safety, environmental protection and flame retardancy, with excellent adhesion to steel substrates and good corrosion resistance.
For fans, axles, automotive chassis, guardrails, hardware and other light industrial metal products.
| Colour | White, or other colours as specified by the customer |
|---|---|
| Volume Solids | 41% |
| Typical dry film thickness | 40 µm |
| Theoretical Spreading Rate | 8.83 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.49 mm; output pressure 12–15 MPa |
| Conventional spray | Recommended: nozzle size 1.3–1.5 mm; output pressure 0.3–0.4 MPa |
| Brush | Recommended for touch-up or small-area application. Take care to achieve the specified dry film thickness. |
| Roller application | Recommended for small-area application. Take care to achieve the specified dry film thickness. |
| Thinner | Clean fresh water |
| Paint equipment cleaner | Clean fresh water |
| Pot life | Unlimited |
| Drying Time | |||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Minimum recoat interval (h) |
| 5°C | 2 | 48 | |
| 23°C | 1 | 24 | |
| 35°C | 0.5 | 12 | |
Note: ventilation, temperature, relative humidity and film thickness all affect drying and curing times. The data above are measured under well-ventilated conditions with relative humidity <75%.
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 6 months |
| Packaging Specifications | 20 kg in a 20 L container |
| density | 1.16 kg/L |
Primed or intermediate-coated surfaces shall be kept clean and dry and free from contamination; the substrate temperature shall be at least 3 °C above the dew point.
Previous coat: alkyd, acrylic, epoxy or polyurethane primers or intermediate coats, or other coating systems verified by testing per customer requirements.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.