AL054 Alkyd Anti-corrosive Primer is an alkyd coating used as a primer. Suitable for corrosion protection of steel structures in C2–C4 atmospheric corrosion environments, with convenient application. One-component, with iron red, zinc oxide, phosphate or molybdate added as anti-corrosive pigments, environmentally friendly and free of lead and chromium heavy metals; the film shows strong adhesion to steel substrates and good anti-corrosive performance, with strong intercoat adhesion to nitrocellulose and alkyd topcoats. Parameters on this page: dry film thickness 50 µm equivalent to 86.2 µm wet film, theoretical spreading rate 8.59 m²/kg, number of components one-component.
Parameter source: OSAKA manufacturer's Technical Data Sheet (TDS) "AL054 Alkyd Anti-corrosive Primer"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 58% |
|---|---|
| Dry Film Thickness | 50 µm corresponds to 86.2 µm WFT |
| Theoretical Spreading Rate | 8.59 m²/kg |
| VOC | 361 g/L |
| Density / Specific Gravity | Approx. 1.35 kg/L |
| Number of Components | One-component |
| Flash Point | 38°C |
| Thinner | OUP 100, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
One-component, with iron red, zinc oxide, phosphate or molybdate added as anti-corrosive pigments, environmentally friendly and free of lead and chromium heavy metals; the film shows strong adhesion to steel substrates and good anti-corrosive performance, with strong intercoat adhesion to nitrocellulose and alkyd topcoats.
Suitable for corrosion protection of steel structures in C2–C4 atmospheric corrosion environments, easy to apply.
| Volume Solids | 58% |
|---|---|
| Dry Film Thickness | 50 µm corresponds to 86.2 µm WFT |
| Theoretical Spreading Rate | 8.59 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 361 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable but not recommended. |
| Thinner | OUP 100, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 100 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 2 | 30 | 30 h | Unlimited |
| 23°C | 1 | 18 | 18 h | Unlimited |
| 35°C | 0.5 | 12 | 12 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| Flash Point | 38°C |
| density | Approx. 1.35 kg/L |
Steel surfaces: abrasive blast clean to Sa 2.5 (ISO 8501:2007) or clean by hand or power tools to St 3. Keep clean and dry.
Shall not be overcoated with epoxy or polyurethane coatings.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.