ACP1005 Water-borne Acrylic Topcoat is a water-borne coating used as a topcoat. It is used for anti-corrosion protection of steel structure surfaces under low to medium C2–C4 atmospheric corrosion environments, and is widely used in automotive chassis, fans, mining machinery, power equipment and construction machinery. A one-component water-borne acrylic topcoat, low VOC, safe and environmentally friendly, with excellent intercoat adhesion to water-borne anti-corrosion primers, good gloss and colour retention, and good weather resistance. Parameters on this page: volume solids 38%–45%, dry film thickness 30 µm, theoretical spreading rate 11.1–12.5 m²/kg.
Parameter source: OSAKA original technical data sheet (TDS) “ACP1005 Water-borne Acrylic Topcoat”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 38%-45% |
|---|---|
| Dry Film Thickness | 30 µm |
| Theoretical Spreading Rate | 11.1–12.5 m²/kg |
| VOC | — |
| Density / Specific Gravity | 1.10–1.20 kg/L |
| Number of Components | One-component |
| Thinner | Clean fresh water |
| Mixing Ratio | Single pack |
| Colour / Appearance | White, black or other colours specified by the customer |
A one-component water-borne acrylic topcoat, low VOC, safe and environmentally friendly, with excellent intercoat adhesion to water-borne anti-corrosion primers, good gloss and colour retention, and good weather resistance. Can air-dry at ambient temperature or be low-temperature baked.
For corrosion protection of steel structures in low to medium atmospheric corrosion environments C2–C4, widely used for automotive chassis, fans, mining machinery, power equipment and construction machinery.
| Colour | White, black or other colours specified by the customer |
|---|---|
| Volume Solids | 38%-45% |
| Typical dry film thickness | 30 µm |
| Theoretical Spreading Rate | 11.1–12.5 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.49 mm; output pressure 12–15 MPa |
| Conventional spray | Recommended: nozzle size 1.3–1.5 mm; output pressure 0.3–0.4 MPa |
| Brush | Recommended for touch-up or small-area application. Take care to achieve the specified dry film thickness. |
| Roller application | Recommended for small-area application. Take care to achieve the specified dry film thickness. |
| Thinner | Clean fresh water |
| Paint equipment cleaner | Clean fresh water |
| Pot life | Unlimited |
| Drying Time | |||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Minimum recoat interval (h) |
| 5°C | 60 | 10 | |
| 23°C | 30 | 5 | |
| 35°C | 10 | 2 | |
Note: ventilation, temperature, relative humidity and film thickness all affect drying and curing times. The data above are measured under well-ventilated conditions with relative humidity <75%.
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 20 kg in a 20 L container |
| density | 1.10–1.20 kg/L |
Primed or intermediate-coated surfaces shall be kept clean and dry and free from contamination; the substrate temperature shall be at least 3 °C above the dew point.
Previous coat: acrylic, polyurethane or epoxy primer or intermediate coat, or other coating systems verified by testing according to customer requirements.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.