HI-ALKYD 6035 Alkyd Topcoat belongs to alkyd coatings and is used as a topcoat. It is used for protective coating of steel structure surfaces such as bridges, petrochemical, power, steel structures, pipelines, equipment and steel frames under medium corrosion environments and below. The product film is tough and glossy, with bright colours and good weather resistance, flexibility, intercoat adhesion and application performance. 1.23 ± 0.1 kg/L (varies slightly with colour) The coating surface shall be clean, dry and free from contamination. Parameters on this page: Volume Solids 50 ± 3%, Dry Film Thickness 30–60 µm, Theoretical Spreading Rate 0.10 kg/m².
Parameter source: Nippon Paint Industrial NIPPON INDUSTRIAL original technical data sheet (TDS) “HI-ALKYD 6035 Alkyd Topcoat”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 50 ± 3% |
|---|---|
| Dry Film Thickness | 30-60µm |
| Theoretical Spreading Rate | 0.10 kg/m² |
| VOC | 416 g/L (white) |
| Density / Specific Gravity | 1.23 ± 0.1 kg/L (varies slightly with colour) |
| Number of Components | One-component |
| Thinner | Thinner 0920 |
| Mixing Ratio | This product is single-component; no mixing is required |
| Colour / Appearance | Various colours (standard industrial colour chart or custom colours) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
HI-ALKYD 6035 is a one-component alkyd enamel based on long-oil alkyd resin. The product film is tough and glossy, with bright colours and good weather resistance, flexibility, intercoat adhesion and application performance.
Used for protective coating of steel structure surfaces such as bridges, petrochemical, power, steel structures, pipelines, equipment and steel frames under medium corrosion environments and below.
| Colour | Various colours (standard industrial colour chart or custom colours) |
|---|---|
| Gloss (60°) | Flat |
| Solids content (by volume) | 50±3% |
| Density | 1.23 ± 0.1 kg/L (varies slightly with colour) |
| VOC | 416 g/L (white) |
The surface to be coated shall be clean, dry and free from contamination. Surface assessment and cleaning shall follow ISO 8504. Oil and
Remove oil and grease in accordance with SSPC-SP1 solvent cleaning.
Blast cleaning to Sa2 (ISO 8501-1:2007) or SSPC-SP6 (or SSPC-SP10 for better results). If the blasted surface oxidises before coating, it shall be re-prepared to the specified standard. Surface defects exposed after blasting shall be treated by grinding, filling or other suitable methods. The surface profile shall be 40–75 µm.
Repair of damaged areas: damaged areas must be abrasive blast cleaned to Sa2½ (ISO 8501-1:2007) or SSPC-SP6 (for ideal performance, blast clean to SSPC-SP10). Where local areas cannot be blast cleaned, mechanical grinding to St3 (ISO 8501-1:2007) is permitted. After surface preparation, primer and topcoat application may proceed in system sequence. Before application, ensure the surface to be coated is clean and dry, and application must be carried out within the specified recoat interval (refer to the relevant product application instructions).
Other surfaces: if the coating is to be applied to other substrates, consult the Protective Coatings Division of Nippon Paint Industrial Coatings.
Application is not recommended when ambient temperature is below 5 °C or above 45 °C, or relative humidity is above 85%; steel plate
The temperature should be at least 3 °C above the dew point of the surrounding air.
| Mixing ratio | This product is single-component; no mixing is required |
|---|---|
| Theoretical spreading rate | 0.10 kg/m² (calculated on 40 µm dry film) |
| Thinner | Thinner 0920: the amount of thinning shall not exceed the range permitted by local regulations. |
Roller/brush/air spray: for touch-up and small-area application;
Airless spray: recommended for large-area application;
Regardless of the method used, the specified dry film thickness must be achieved.
| Air Spray | Nozzle size: 1–2 mm; air pressure: 0.3–0.5 MPa |
|---|---|
| Airless Spray | Tip size: 0.017"–0.021"; nozzle pressure: 120–150 kg/cm² |
| Typical film thickness | 30–60 µm DFT : 73–146 µm WFT — drying time |
| Substrate Temperature | 15°C | 25°C | 40°C |
| Touch dry time | 4h | 2h | 1h |
| Hard dry time | 48h | 24h | 12h |
| Fully cured | 14d | 7d | |
| Minimum recoat time | 48h | 24h | 12h |
| Maximum recoat time* | - | ||
Note: *the surface must be free of chalking and contamination before recoating. Prolonged outdoor exposure, a smooth surface or contamination adversely affects recoat adhesion; the surface must therefore be roughened, sweep blasted or high-pressure water jetted to ensure adequate adhesion.
The data above are for guidance only. Actual recoat and drying times may be shorter or longer depending on film thickness, ventilation, humidity, coating system, and prior hand or mechanical preparation conditions.
The following primers/topcoats are recommended for use with HI-ALKYD 6035 Alkyd Topcoat
Primer
Select the coating system according to the specific requirements; refer to the product manual or contact Nippon Paint for professional guidance.
Packaging Pack Weight Package size 20 kg 20 kg 18 L
| Storage; shelf life (from date of production) | 12 months (25 °C) |
|---|
The product shall be stored in a cool, dry, ventilated warehouse meeting fire safety requirements, with warehouse temperature not exceeding 40 °C. The above is the minimum shelf life; beyond this period, testing is required to determine whether continued use is acceptable.
Due to the nature of alkyd products, skinning tends to occur after long-term storage. If skinning occurs, simply remove the skin; the product can still be used normally.
Safety information.
All information in this product data sheet is based on laboratory tests and practical experience. However, since the product is subject to many unforeseeable and uncontrollable factors in actual use, we guarantee only the quality of the product itself. Read this data sheet carefully and confirm with Nippon Paint that it is the latest version before using the product.
We reserve the right to modify this product data sheet without prior notice.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.