This product features self-indicating SI technology, enabling the painter to visually check during application whether the film thickness (wet film/dry film) reaches the specified thickness. Parameters on this page: volume solids 98–100%, theoretical spreading rate 3.33 m²/L, number of components two-component.
Parameter source: nippon-marin original technical data sheet (TDS) “NOA 1000 FWT SF Noah Solvent-free Potable Water Tank Epoxy Coating”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 98-100% |
|---|---|
| Dry Film Thickness | 300µm |
| Theoretical Spreading Rate | 3.33 m²/ℓ |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | No thinning required; for cleaning use THINNER 600 |
| Mixing Ratio | Base : curing agent = 12.5 : 3.5 |
| Colour / Appearance | Yellow base — LEF358, curing agent — LEF601 |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
High-performance two-component solvent-free pure epoxy anti-corrosive coating for potable water tanks; being solvent-free, application is more hygienic and safer. This product features self-indicating SI technology, enabling the painter to visually check during application whether the film thickness (wet film/dry film) reaches the specified thickness.
Potable Water Tank Coating
| Type | Solvent-free pure epoxy (two-component) |
|---|---|
| Colour | Yellow base — LEF358, curing agent — LEF601 |
| Gloss | Semi-gloss |
| Solids content (by volume) | 98 ~ 100% (ISO3233:1998) |
| Mixing ratio (by volume) | Base : curing agent = 12.5 : 3.5 |
| Recommended film thickness | Dry film: 300 µm |
| Wet film | 300µm |
| Theoretical Spreading Rate | 3.33 m²/ℓ |
| Thinner | No thinning required; for cleaning use THINNER 600 |
| 5°C | 20°C | 30°C | ||
| Drying Time | Surface Dry | 48 h | 18 h | 12 h |
| Hard Dry | 5 days | 32 h | 24 h | |
| Recoat interval | Minimum | 5 days | 32 h | 24 h |
| (self-recoat) | Maximum | 10 days | 7 days | 5 days |
| Pot life | 2 h | 1.5 h | 1 h |
| Flash Point | Base 138 °C, Hardener 132 °C |
|---|
Airless Spray Nozzle Tip Size: 0.48–0.53 mm
| Spray fan angle | 45–60° (repair: 30°) |
|---|---|
| Output pressure | 150 ~ 250 kg/㎝2 |
| Brush | For small-area repair only |
Blast clean to ISO-Sa2.5 or power tool clean to ISO-St3.0. All surfaces to be coated shall be clean, dry and free from contaminants. High-pressure fresh water washing to remove all grease, soluble salts and foreign matter.
| Packaging Specifications | 16 L (Base 12.5 L, Hardener 3.5 L) |
|---|
Although this product contains no solvent, the necessary protective measures are still recommended, such as: gloves, protective
1) The content of this product data sheet may be changed at any time as experience is gained and the product is further developed 2) No thinning is required; cleaning may be carried out with NIPPON MARINE THINNER 600 3) At temperatures below 10 °C, curing slows; if necessary, hot air heating may be used to accelerate curing.
4) The pot life of this product is significantly shorter than that of solvent-borne paints; prepare the paint according to the quantity required 5) Provide adequate ventilation during and after application 6) For coating application matters, refer to "NOA 1000 FWT SF Potable Water Tank Coating Application Specification" 7) Allow at least 7 days (23 °C) of drying before loading potable water 8) Store in the paint warehouse
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.