NIPPON U-MARINE FINISH H topsides topcoat belongs to topcoats. Parameters on this page: dry film thickness 40-60 µm, theoretical spreading rate 13.00 m²/L.
Parameter source: nippon-marin original technical data sheet (TDS) NIPPON U-MARINE FINISH H Hull Topcoat; values such as spreading rate are converted from TDS parameters for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | — |
|---|---|
| Dry Film Thickness | 40-60 µm |
| Theoretical Spreading Rate | 13.00 m2/L |
| VOC | 298 g/L |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | THINNER 700 |
| Mixing Ratio | By volume:Base 8.5 / Hardener 1 |
| Colour / Appearance | White, Black, Other colours |
A two pack, acrylic polyurethane topcoat with high solid, high coverage, giving excellent weathering resistance and color/gloss retention, as well as long term recoatablity.
Finish for topsides, superstructures, etc.
| Type | Polyurethane (High build / Two-pack) |
|---|---|
| Color | White, Black, Other colours |
| Gloss | High-gloss |
| Volume Solid | 65 ± 2% (ISO3233:1998) |
| Dry Film Thickness | 40 ~ 60 µm |
| Wet Film Thickness | 62 ~ 92 µm |
| Theoretical Coverage | 13.00 m2/ L (50 µm) Drying Time |
30mintues (20°C) 10mintues (30°C)
| Surface Dry Dry hard | 40 minutes (5°C) 16hours (5°C) 8hours (20°C) | 40 minutes (5°C) 6hours (30°C) |
| Full cure | 14days (5°C) 7days (20°C) | 5days (30°C) |
Interval before Overcoating(by self)
| Min. | 16hours (5°C) |
|---|---|
| 8hours (20°C) | 6hours (30°C) |
| Max. | -- (5°C) -- (20°C) -- (30°C) |
The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.
| VOC | 298 g/L (GB/T 23985-2009) |
|---|---|
| Thinner | THINNER 700 |
Airless Spray
| Tip range | 0.38 ~ 0.48 mm |
|---|---|
| Fan angle | 55° ~ 60° |
| Output pressure | 120 ~ 150 kg / cm2 |
| Brush/Roller | For touching up small areas only |
| Mixing Ratio | By volume:Base 8.5 / Hardener 1 |
| Pot Life after Mixing | 6hours (5°C) 3hours (20°C) |
2hours (30°C)
| Packaging | Two Packs: 20L(Base 17.9 L, Hardener 2.1 L) Package may vary from country to country. |
|---|---|
| Flash Point | Base:32.5°C,Hardener:28°C (GB/T 5208-2008) |
| Shelf life | Base:18 months/25°C,Hardener:18 months/25°C |
Storage must be in accordance with national regulations, tightly closed in container in a dry, cool and well-ventilated space, keep away from sources of heat and ignition. Too high temperature will shorten the shelf life or even gel in the tank. The above shelf life is the shortest time, and must be tested to determine if it can continue to be used when storage time is beyond the shelf life.
All surfaces to be coated should be clean, dry and free from chalking and contamination. Adhesion will be negatively influenced if film is exposed outside for long time and causes smooth or contaminated surface. Film must be roughened, sweep blasted or treated by high pressure water jetting to achieve required adhesion.
High pressure fresh water wash and remove all oil / grease, soluble contaminants and other foreign matters.
Take precautions to avoid skin and eye contact (i.e. gloves, goggles, face masks, barrier creams etc.) Proper ventilation and protective measures must be provided during applications and drying period to keep solvent vapour concentrations within safe limits.
Prior to use, obtain, consult and follow the SDS for this product concerning health and safety information.
| 1. | The information contained in this sheet is liable to modification from time to time in the light of experience and our policy of continuous product development. |
|---|---|
| 2. | For availability of product consult Nippon Paint Marine representatives. |
| 3. | Unit size and filled volumes can vary due to local regulations. |
| 4. | Use products that comply with local regulations to clean the paint equipment |
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.