NIPPON E-MARINE PRIMER GALVA primer for galvanised steel belongs to primers. Parameters on this page: volume solids 52 ± 2%, dry film thickness 20-40 µm, theoretical spreading rate 17.33 m²/L.
Source of parameters: nippon-marin original technical data sheet (TDS) 'NIPPON E-MARINE PRIMER GALVA Galvanized Parts Primer'; values such as spreading rate are converted from TDS parameters and are for model selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 52 ± 2% |
|---|---|
| Dry Film Thickness | 20-40 µm |
| Theoretical Spreading Rate | 17.33 m²/L (30 µm) |
| VOC | 418 g / L as supplied |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | NIPPON MARINE THINNER 600 / NIPPON … |
| Mixing Ratio | BASE 6.2 / HARDENER 1 |
| Colour / Appearance | White |
A two-pack epoxy paint which can be directly applied to nonferrous metal surface (aluminum, galvanized steel, stainless steel and alloy). With excellent adhesion and resistance to water, it can be overcoated with various kinds of finishes.
Primer for nonferrous metal surface (galvanized, aluminum, and stainless)
| Type | Pure epoxy (Two-pack) |
|---|---|
| Color | White |
| Gloss | Flat |
| Volume Solids | 52 ± 2% (ISO3233:1998) |
| Typical Dry Film Thickness | 20 ~ 40 µm |
| Approx. Wet Film Thickness | 39 ~ 77 µm |
| Theoretical Coverage | 17.33 m²/L (30 µm) |
| Drying Time | Surface Dry | 30 minutes (5°C) | 10 minutes(20°C) | 5 minutes (30°C) |
| Dry Hard | 8 hours (5°C) | 4 hours (20°C) | 3 hours (30°C) | |
| Full Cure | 14 days (5°C) | 7 days (20°C) | 5 days (30°C) | |
| Interval before Overcoating | Min. | 8 hours (5°C) | 4 hours (20°C) | 3 hours (30°C) |
| (by self) | Max. | ― (5°C) | ― (20°C) | ― (30°C) |
| VOC Values | 418 g / L as supplied |
|---|---|
| Thinner | NIPPON MARINE THINNER 600 / NIPPON MARINE THINNER 615 (China Regions) |
| Mixing Ratio by Volume | BASE 6.2 / HARDENER 1 |
| Pot Life after Mixing | 18 hours (5°C) |
| 8 hours (20°C) | 5 hour (30°C) |
| Packaging | Two Packs |
| Japan Local Brand | NIPPON E-MARINE PRIMER GALVA |
| Flash Point | BASE 28°C, HARDENER 25°C |
For non ferrous surface, solvent cleaning is recommended.
For rusted part on ferrous surface, power tool cleaned to ISO-St 3 is recommended.
Take precautions to avoid skin and eye contact (i.e. gloves, goggles, face masks, barrier creams etc.) Proper ventilation and protective measures must be provided during applications and drying period to keep solvent vapor concentrations within safe limits.
Prior to use, obtain, consult and follow the SDS for this product concerning health and safety information.
1)The information contained in this sheet is liable to modification from time to time in the light of experience and our policy of continuous product development.
2) At temperature below 5°C, it will take longer to dry and harden.
3) Consult Nippon Paint Marine Coatings in advance when polyurethane paint is overcoated.
4) It is applicable to steel substrate.
5) For availability of product consult Nippon Paint Marine representatives.
6) Unit size and filled volumes can vary due to local regulations.
7) Use products that comply with local regulations to clean the paint equipment.
8) Store the paints in paint store.