NIPPON E-MARINE FINISH M topsides topcoat belongs to topcoats. Parameters on this page: volume solids 62 ± 2%, dry film thickness 40-125 µm, theoretical spreading rate 10.33 m²/L.
Source: NIPPON MARINE original technical data sheet (TDS) "NIPPON E-MARINE FINISH M Hull Topcoat"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 62 ± 2% |
|---|---|
| Dry Film Thickness | 40-125 µm |
| Theoretical Spreading Rate | 10.33 m²/L (60 µm) |
| VOC | 380 g / L as supplied |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | NIPPON MARINE THINNER 600 / NIPPON … |
| Mixing Ratio | BASE 80 / HARDENER 20 |
| Colour / Appearance | White, Black, 445 Red Oxide, and a … |
A two-pack pure epoxy finish for offshore structures, above water hulls, decks and superstructures.
An interval-free system is realized when combined with NIPPON E-MARINE PRIMER.
Finish for boottop, topsides, decks, holds, superstructures, offshore structures, etc.
| Type | Pure epoxy (Two-pack) |
|---|---|
| Color | White, Black, 445 Red Oxide, and a wide range of other colors |
| Gloss | Semi-gloss |
| Volume Solids | 62 ± 2% (ISO3233:1998) |
| Typical Dry Film Thickness | 40 ~ 125 µm |
| Approx. Wet Film Thickness | 65 ~ 202 µm |
| Theoretical Coverage | 10.33 m²/L (60 µm) |
| Drying Time | Surface Dry | 3 hours (5°C) | 1.5 hours (20°C) | 1 hour (30°C) |
| Dry Hard | 32 hours (5°C) | 16 hours (20°C) | 12 hours (30°C) | |
| Full Cure | 14 days (5°C) | 7 days (20°C) | 5 days (30°C) | |
| Interval before Overcoating | Min. | 32 hours (5°C) | 16 hours (20°C) | 12 hours (30°C) |
| (by self) | Max. | ― (5°C) | ― (20°C) | ― (30°C) |
| VOC Values | 380 g / L as supplied |
|---|---|
| Thinner | NIPPON MARINE THINNER 600 / NIPPON MARINE THINNER 615 (China Regions) |
Airless Spray
| Tip range | 0.48 ~ 0.53 mm |
|---|---|
| Fan angle | 55° ~ 69° |
| Output pressure | 100 ~ 150 kg/cm² |
| Brush | For touching up small areas only |
| Mixing Ratio by Volume | BASE 80 / HARDENER 20 |
| Pot Life after Mixing | 16 hours (5°C) |
| 8 hours (20°C) | 5 hours (30°C) |
| Packaging | Two Packs |
| Japan Local Brand | NIPPE EPOXY FINISH M |
| Flash Point | BASE 28.5 °C, HARDENER 28.5 °C |
All surfaces to be coated should be clean, dry and free from contamination.
High pressure fresh water wash and remove all oil / grease, soluble contaminants and other foreign matters.
Take precautions to avoid skin and eye contact (i.e. gloves, goggles, face masks, barrier creams etc.) Proper ventilation and protective measures must be provided during applications and drying period to keep solvent vapor concentrations within safe limits.
Prior to use, obtain, consult and follow the SDS for this product concerning health and safety information.
| 1) | The information contained in this sheet is liable to modification from time to time in the light of experience and our policy of continuous product development. |
|---|---|
| 2) | At temperatures below 5°C, the coating will take longer to dry and harden. |
| 3) | Intercoat adhesion is good at any interval. However, salt will deteriorate the adhesion and should be removed before application of subsequent coats. |
| 4) | Ventilate well in the areas with insufficient air flow. |
| 5) | If dusting may occur during application at high temperatures, use NIPPON MARINE THINNER 650. |
| 6) | Use NON-SLIP SAND to produce a non-slip surface for decks and walkways. |
| 7) | When gloss & colour retention is to be required, NIPPON U-MARINE FINISH is recommended. |
| 8) | For availability of product consult Nippon Paint Marine representatives. |
| 9) | Unit size and filled volumes can vary due to local regulations. |
10) Use products that comply with local regulations to clean the paint equipment.
11) Store the paints in paint store.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.