A general anti-corrosion paint for various areas (hull underwater parts, waterline, freeboard, deck, cargo hold, ballast tank, etc.). E-MARINE A/C LT is a two-component, high-solids, low-VOC (volatile organic compounds) general-purpose epoxy primer; it is the winter type of E-MARINE A/C. This product has excellent abrasion resistance, water resistance, seawater resistance and anti-corrosion electrical resistance, so it is suitable for almost all areas such as hull underwater parts, waterline, freeboard, deck, cargo hold, ballast tank, etc. Parameters on this page: volume solids 74 ± 2%, theoretical spreading rate 4.23 m²/L (dry film 175 µm), components two-component.
Data source: nippon-marin original Technical Data Sheet (TDS), "NIPPON E-MARINE A/C LT Epoxy Anti-rust Primer Winter Type"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 74 ± 2% |
|---|---|
| Dry Film Thickness | 125µm ~250µm |
| Theoretical Spreading Rate | 4.23 m²/L (dry film 175 µm) |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | THINNER 600 (thinning by weight: 0–10%) |
| Mixing Ratio | Base : curing agent = 16 : 4 |
| Colour / Appearance | Red-brown base – CFD143 Grey base – CFD637 Hardener – … |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
E-MARINE A/C LT is a two-component, high-solids, low-VOC (volatile organic compounds) general-purpose epoxy primer; it is the winter type of E-MARINE A/C. This product has excellent abrasion resistance, water resistance, seawater resistance and anti-corrosion electrical resistance, so it is suitable for almost all areas such as hull underwater parts, waterline, freeboard, deck, cargo hold, ballast tank, etc. It can be used with various topcoats.
A general-purpose anticorrosive coating for various areas (underwater hull, waterline, topsides, decks, cargo holds, ballast tanks and others)
| Type | Epoxy (low-temperature winter type / abrasion-resistant / high-build / two-component) |
|---|---|
| Colour | Red-brown base – CFD143 Grey base – CFD637 Hardener – CFZ410 |
| Gloss | Semi-gloss |
| Solids content (by volume) | 74 ± 2% (ISO3233:1998) |
| Mixing ratio (by volume) | Base : curing agent = 16 : 4 |
| Recommended film thickness | DFT: 125–250 µm |
| Wet film | 169µm ~ 338µm |
| Theoretical Spreading Rate | 4.23 m²/L (dry film 175 µm) |
| Thinner | THINNER 600 (thinning by weight: 0–10%) |
| 5°C | 10°C | 20°C | ||
| Drying Time | Surface Dry | 1 h | 40 min | 20 min |
| Hard Dry | 24 h | 16 h | 10 h | |
| Fully cured | 10 days | 7 days | 5 days | |
| Recoat interval | Minimum | 24 h | 16 h | 10 h |
| (Self-overcoating: immersed areas) | Maximum | 30 days | 14 days | |
| Recoat interval | Minimum | 24 h | 16 h | 10 h |
| (Self-overcoating: exposed areas) | Maximum | --- | --- | |
| Pot life | 4 h | 3 h | 2 h |
| Flash Point | Base 29 °C, hardener 25 °C |
|---|
Airless spray; gun tip size: 0.48–0.59 mm
| Spray fan angle | 55–62°, (repair: 30°) |
|---|---|
| Output pressure | 150-200 kg/㎝2 |
| Brush | For small-area repair only |
Blast clean to ISO Sa2.5 or power-tool clean to ISO St3
| Packaging Specifications | 20 L (base 16 L, curing agent 4 L) |
|---|
Take the necessary protective measures to avoid skin and eye contact (e.g. gloves, safety glasses, face shield, barrier cream). Ensure adequate ventilation during application and drying to keep solvent vapour concentrations within safe limits.
Before use, refer to the health and safety information in the Material Safety Data Sheet (MSDS) for this product.
1) The content of this data sheet may be revised at any time as experience grows and the product develops. 2) Below 5 °C, drying and curing times are extended. 3) At high temperatures, spray mist is easily produced during application; use THINNER 650. 4) Store in a paint warehouse.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.