Anticorrosive coating for tie-coat sealing at vessel shell (including waterline and freeboard), deck, superstructure and similar areas. The system formed with E-MARINE A/C exhibits excellent seawater resistance and adhesion, and can be used with various antifouling coatings and topcoats. Parameters on this page: volume solids 57 ± 2%, theoretical spreading rate 7.6 m²/L (DFT 75 µm), number of components two-component.
Parameter source: Nippon Paint Marine original technical data sheet (TDS) “NIPPON E-MARINE A/C II Epoxy Tie Coat”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 57 ± 2% |
|---|---|
| Dry Film Thickness | 50-125µm |
| Theoretical Spreading Rate | 7.6 m²/L (DFT 75 µm) |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | THINNER 600 (thinning by weight: 0–10%) |
| Mixing Ratio | Base : curing agent = 16:4 |
| Colour / Appearance | Grey base — CHA637 Cream base — CFZ335 Curing agent — … |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Two-component epoxy anti-corrosive tie-coat/sealer. Health, safety and environmental factors were fully considered in product design. The system composed with E-MARINE A/C exhibits excellent seawater resistance and adhesion, and can be used with various antifouling paints and topcoats.
Anti-corrosive tie-coat/sealer for ship shell (including waterline and freeboard), deck, superstructure and other areas
| Type | Epoxy resin (two-component/thick-film type) |
|---|---|
| Colour | Grey base — CHA637 Cream yellow base — CFZ335 Curing agent — CHA206 |
| Gloss | Flat |
| Solids content (by volume) | 57± 2% (ISO3233:1998) |
| Mixing ratio (by volume) | Base : curing agent = 16:4 |
| Recommended film thickness | Dry film: 50–125 µm |
| Wet film | 88 ~ 219µm |
| Theoretical Spreading Rate | 7.6 m²/L (dry film 75 µm) |
| Thinner | THINNER 600 (thinning by weight: 0–10%) |
| 5°C* | 20°C | 30°C | ||
| Drying Time | Surface Dry | 3 h | 1 h | 30 min |
| Hard Dry | 16 h | 8 h | 6 h | |
| Fully cured | 7 days | 5 days | 3 days | |
| Recoat interval | Minimum | 16 h | 8 h | 6 h |
| (self-recoat) | Maximum | ---- | ---- | |
| Pot life | 5 h | 3 h | 2 h |
| Flash Point | Base 29 °C, curing agent 19 °C |
|---|
Airless spray; gun tip size: 0.48–0.59 mm
| Spray fan angle | 55–62°, (repair: 30°) |
|---|---|
| Output pressure | 150-200 kg/㎝2 |
| Brush | For small-area repair only |
All surfaces to be coated must be clean, dry and free of contaminants. Wash with high-pressure fresh water to remove all oil, grease, soluble salts and foreign matter
| Packaging Specifications | 20 L (base 16 L, curing agent 4 L) |
|---|
Take the necessary protective measures to avoid skin and eye contact (e.g. gloves, safety glasses, face shield).
Before use, refer to the health and safety information in the Material Safety Data Sheet (MSDS) for this product.
1) The content of this product data sheet may be changed at any time as experience increases and product development continues. 2) Before recoating, obvious chalking layers, salts and other deposits must be removed by water washing.
3) Store in the paint warehouse.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.