A general-purpose anti-corrosive coating for all areas (hull below waterline, boottop, topside, deck, cargo hold, ballast tank, etc.). A two-component, high-solids, low-VOC general-purpose epoxy primer; the coating offers abrasion resistance, water and seawater resistance, and cathodic protection, making it suitable for nearly all areas including the hull below waterline, boottop, topside, deck, cargo hold and ballast tank. Parameters on this page: volume solids 74 ± 2%; theoretical spreading rate 4.23 m²/L (at 175 µm DFT); number of components: two.
Source: NIPPON MARINE original technical data sheet (TDS) 'NIPPON E-MARINE A/C Epoxy Anti-corrosive Primer'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 74 ± 2% |
|---|---|
| Dry Film Thickness | 125µm ~250µm |
| Theoretical Spreading Rate | 4.23 m²/L (dry film 175 µm) |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | THINNER 600 (thinning by weight: 0–10%) |
| Mixing Ratio | Base : curing agent = 16 : 4 |
| Colour / Appearance | Iron red base – CFC143; grey base – CFC060; hardener – … |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A two-component, high-solids, low-VOC general-purpose epoxy primer; the coating offers abrasion resistance, water and seawater resistance, and cathodic protection, making it suitable for nearly all areas including the hull below waterline, boottop, topside, deck, cargo hold and ballast tank. Compatible with various topcoats.
A general-purpose anticorrosive coating for various areas (underwater hull, waterline, topsides, decks, cargo holds, ballast tanks and others)
| Type | Epoxy (abrasion-resistant/high-build/two-component) |
|---|---|
| Colour | Iron red base – CFC143; grey base – CFC060; hardener – CFC205 |
| Gloss | Semi-gloss |
| Solids content (by volume) | 74 ± 2% (ISO3233:1998) |
| Mixing ratio (by volume) | Base : curing agent = 16 : 4 |
| Recommended film thickness | DFT: 125–250 µm |
| Wet film | 169µm ~ 338µm |
| Theoretical Spreading Rate | 4.23 m²/L (dry film 175 µm) |
| Thinner | THINNER 600 (thinning by weight: 0–10%) |
| 5°C | 20°C | 30°C | ||
| Drying Time | Surface Dry | 3 h | 2 h | 1 h |
| Hard Dry | 47 h | 16 h | 10 h | |
| Fully cured | 14 days | 7 days | 5 days | |
| Recoat interval | Minimum | 47 h | 16 h | 10 h |
| (Self-overcoating: immersed areas) | Maximum | 30 days | 14 days | |
| Recoat interval | Minimum | 47 h | 16 h | 10 h |
| (Self-overcoating: exposed areas) | Maximum | --- | --- | |
| Pot life | 6 h | 4 h | 3 h |
| Flash Point | Base 30 °C, hardener 30 °C |
|---|
Airless spray; gun tip size: 0.48–0.59 mm
| Spray fan angle | 55–62°, (repair: 30°) |
|---|---|
| Output pressure | 150-200 kg/㎝2 |
| Brush | For small-area repair only |
Blast clean to ISO Sa2.5 or power-tool clean to ISO St3
| Packaging Specifications | 20 L (base 16 L, curing agent 4 L) |
|---|
Take the necessary protective measures to avoid skin and eye contact (e.g. gloves, safety glasses, face shield).
Before use, refer to the health and safety information in the Material Safety Data Sheet (MSDS) for this product.
1) The content of this data sheet may be revised at any time as experience grows and the product develops. 2) Below 5 °C, drying and curing times are extended. 3) At high temperatures, spray mist is easily produced during application; use THINNER 650. 4) Store in a paint warehouse.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.