Used for corrosion protection of cargo holds (wet/dry), decks, superstructures, engine rooms, pump rooms, void spaces, cofferdams and other areas. A high-build, high-solids epoxy resin coating with good water resistance, chemical resistance, abrasion resistance and anticorrosive performance. Parameters on this page: volume solids 72 ± 2%, theoretical spreading rate 3.60 m²/L (200 µm), number of components: two-component.
Parameter source: Nippon Marine original technical data sheet (TDS) for NIPPON E-MARINE 400 HS Epoxy 400 HS; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 72 ± 2% |
|---|---|
| Dry Film Thickness | 80-250µm |
| Theoretical Spreading Rate | 3.60 m²/ℓ (200µm) |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | THINNER 600 (0–10%, by weight) |
| Mixing Ratio | Base : curing agent = 15.8 : 4.2 |
| Colour / Appearance | Iron red base – GMJ445 Grey base – GMN060 White base – … |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A high-build, high-solids epoxy resin coating with good water resistance, chemical resistance, abrasion resistance and anticorrosive performance. It does not whiten from night-time condensation, has good low-temperature drying properties, and can be used in all seasons. When recoated with itself, this coating has no maximum recoating interval.
Used for corrosion protection of cargo holds (wet/dry), decks, superstructures, engine rooms, pump rooms, void spaces, cofferdams and other areas
| Type | Epoxy (high-build/high-solids/two-component) |
|---|---|
| Colour | Iron red base – GMJ445 Grey base – GMN060 White base – GMN095 Curing agent – GMA317 |
| Gloss | Flat |
| Solids content (by volume) | 72 ± 2% (ISO3233:1998) |
| Mixing ratio (by volume) | Base : curing agent = 15.8 : 4.2 |
| Recommended film thickness | Dry film: 80 ~ 250 µm |
| Wet film | 111 ~ 347µm |
| Theoretical Spreading Rate | 3.60 m²/ℓ (200µm) |
| Thinner | THINNER 600 (0–10%, by weight) |
| 5°C | 20°C | 30°C | ||
| Drying Time | Surface Dry | 2 h | 1 h | 40 min |
| Hard Dry | 20 h | 7 h | 5 h | |
| Fully cured | 10 days | 6 days | 5 days | |
| Recoat interval | Minimum | 20 h | 7 h | 5 h |
| (self-recoat) | Maximum | ----- | ----- | |
| Pot life | 5 h | 3 h | 2 h |
| Flash Point | Base 29 °C, curing agent 17 °C |
|---|
Airless spray; gun tip size: 0.48–0.59 mm
| Spray fan angle | 55~ 62°, |
|---|---|
| (repair) | 30° |
| Output pressure | 150-200 kg/㎝2 |
| Brush | For small-area repair only |
Blast clean to ISO Sa 2.5 or prepare to ISO St 3.0 by power tool
| Packaging Specifications | 20 L (base 15.8 L, curing agent 4.2 L) |
|---|
Take the necessary protective measures to avoid skin and eye contact (e.g. gloves, safety glasses, face shield).
Before use, refer to the health and safety information in the Material Safety Data Sheet (MSDS) for this product.
1) The content of this data sheet is subject to modification at any time based on our practical experience and the company's subsequent product development strategy.
2) When applying a topcoat over the E-Marine 400 HS coating, remove the chalked layer, salt and other foreign matter from the surface by high-pressure water washing or other methods.
3) For wood chip carriers, a single-coat system is basically used.
4) Store in a paint warehouse.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.