PU FINISH CT-50 Polyurethane Topcoat CT-50 is a polyurethane coating used as a topcoat. Outdoor Corrosion Resistant suitable for UL 50E enclosures. For new construction or as a maintenance topcoat, for special containers and similar. A high-gloss high-performance polyurethane topcoat for heavy-duty anti-corrosion metal surfaces. Specifications on this page: theoretical spreading rate 0.021 kg/m²/10 µm, number of components: two-component. Comparable products of the same brand and type: PU FINISH 2010 Polyurethane 2010 Topcoat, PU FINISH HD-25 Polyurethane Topcoat HD-25, PU FINISH HS-50 Polyurethane Topcoat HS-50.
Source: KANSAI original technical data sheet (TDS) 'PU FINISH CT-50 Polyurethane Topcoat CT-50'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 63% |
|---|---|
| Dry Film Thickness | 30–80 µm per coat |
| Theoretical Spreading Rate | 0.021 kg/m² per 10 µm |
| VOC | ≤ 340 g/L, complying with EU Solvent Emissions Directive 2004/42/EC, subcategory j |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Flash Point | Above 23 °C |
| Thinner | Polyurethane thinner |
| Mixing Ratio | Base/Hardener=8/1(by weight) |
| PU FINISH CT-50 | Polyurethane Topcoat CT-50 |
|---|
A high gloss durable finish based on polyurethane for steel surfaces of heavy-duty.
As a finish can be used in new construction situations and as maintenance finish for special
UL50E certified
Outstanding weathering resistance and gloss retention
| Color | White and Colors |
|---|---|
| Colour | White and various colours |
| Gloss | High Gloss |
| Gloss | High gloss |
| Volume Solids | 63% |
| VOC | ≤340g/L,accord with EU Dircrtive2004/42/EC,subcategory j |
| Volatile organic compound content | ≤ 340 g/L, complying with EU Solvent Emissions Directive 2004/42/EC, subcategory j |
| Flash Point | Above 23 °C |
| Film thickness | Dry 30-80microns/coat Wet : 50-130microns/coat |
| Applied film thickness | Dry film: 30–80 µm per coat; wet film: 50–130 µm per coat |
| Theoretical Coverage | 0.021kg/m²/10 microns |
| Theoretical Spreading Rate | 0.021 kg/m² per 10 µm |
Practical coverage depending on surface conditions, environment, applications, etc.
| Application Temperature | -5°C-40°C |
|---|---|
| Mixing | Combine Base with Hardener, mix thoroughly with power agitator |
| Mixing | Mix the base and curing agent and stir thoroughly with a power tool |
| Mixing Ratio | Base/Hardener=8/1(by weight) |
| Mixing ratio | Base : curing agent = 8:1 (by weight) |
| Pot Life | 5°C | 10°C | 20°C | 30°C |
| Pot life | 8hrs | 6hrs | 5hrs | 3hrs |
| Application Methods | Airless spray, air spray, brush and roller |
|---|---|
| Application Methods | Airless spray, air spray, brush, roller |
| Nozzle tip | Nozzle size | 0.33mm-0.43mm |
| Nozzle pressure | Output pressure | ≥10MPa |
| Thinning ratio | 0–10% by weight |
Brush/Roller; Thinning ratio 0–10% by weight
| Thinner | Retan Thinner |
|---|---|
| Thinner | Polyurethane thinner |
| Drying time & Overcoating interval | Drying time & Surface dry | Drying time & touch dry | -5°C 4hrs | 0°C 2hrs | 10°C 1.5hrs | 20°C 1hrs | 30°C 1hrs |
| Drying time & recoat interval | Touch dry | Semi-hard dry | 24hrs | 16hrs | 12hrs | 10hrs | 6hrs |
| Min. interval | Minimum recoat interval | 30hrs | 24hrs | 20hrs | 16hrs | 12hrs | |
| Max. interval | Maximum recoat interval | - | |||||
| Typical undercoat | EPOTAINER EX(M) or according to the coating systems of Kansai |
|---|---|
| Suitable for undercoating | Epoxy MIO high-build paint EX(M), or refer to the company's recommended system |
The information given on this sheet is to the best of our knowledge and accurate at the time of
issuing. Since conditions of use are beyond the manufacturer’s control, information contained herein is without warranty, implied or otherwise, and the suitability of the material for the use contemplated is the sole responsibility of the buyer. The information contained on this data sheet is subject to modification at any time due to our policy of modification and product development.Please check this date sheet is current prior to using the product.
The information provided in this data sheet is, to the best of our knowledge, the most complete and accurate information currently available. As the conditions of product use are beyond our control, this information carries no warranty, and we are responsible to the buyer only in the selection of the product. As our products and production processes are continuously developed, the content of this data sheet is subject to change at any time, and all information herein is subject to our confirmation. Confirm that the data sheet in hand is the latest version before using the product.
| Issued Date | 2023/9 |
|---|
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.