EPOTECT EX is an epoxy coating. Used in newbuilding projects, as a primer or intermediate coat. It is a low-VOC, high-solids, two-component high-build epoxy coating. Parameters on this page: volume solids 76 ± 2%, dry film thickness 75-200 µm/coat, theoretical spreading rate 6.08 m²/L. Comparable models from the same brand: EPOFEND AR 80 high-strength abrasion-resistant epoxy high-build, EPOFEND AR abrasion-resistant epoxy, EPOFEND MT-30 special epoxy MT-30.
Parameter source: KANSAI original technical data sheet (TDS) for EPOTECT EX Issue Date; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 76 ± 2% |
|---|---|
| Dry Film Thickness | 75–200 µm per coat |
| Theoretical Spreading Rate | 6.08 m²/L / 125 µm |
| VOC | 256 g/L, complying with EU Solvent Emissions Directive 2004/42/EC, subcategory j |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Flash Point | Above 20 °C |
| Thinner | 30°C |
| Mixing Ratio | Base/Hardener=9/1(by weight) |
| Application Methods | Airless spray, air spray, brush and roller |
|---|
| Nozzle tip | Nozzle size | 0.43mm-0.53mm |
| Nozzle pressure | Output pressure | ≥15Mpa |
| Thinning ratio | 0–10% by volume |
Epomarine Thinner #20
| Thinner | Epoxy Thinner #20 |
|---|
| Thinner | Temperature | 5°C | 10°C | 20°C | 30°C | |
| Drying time & | Surface dry | Touch dry | 5hrs | 4hrs | 3hrs | 2hrs |
| Overcoating interval | Touch dry | Semi-hard dry | 48hrs | 24hrs | 16hrs | 12hrs |
| Drying time & recoat interval | Min. interval | Minimum recoat interval | 48hrs | 36hrs | 24hrs | 16hrs |
| Max. interval | Maximum recoat interval | 7days | ||||
Bare steel
| Applied Substrate | Bare steel |
|---|---|
| Suitable substrates | SD Zinc 500, Epofend Zinc 60 etc. |
| Typical undercoat | Epoxy zinc-rich coating 500, epoxy zinc-rich 60, and similar |
| Suitable for undercoating | Retan 6000, Kanpe Flon HD or according to the coating system of COSCO Kansai. |
| Typical topcoat; suitable overcoat | Polyurethane Topcoat 6000, fluorocarbon topcoat, or refer to our coating system |
Store in dry, cool condition and away from sources of heat and ignition. Containers must be kept
The information given on this sheet is to the best of our knowledge and accurate at the time of
A low VOC, high solids, two pack high build epoxy coating
As a primer or intermediate coat can be used in new building and repair vessel .
Low VOC, high volume solids
| Color | Grey |
|---|---|
| Colour | Grey |
| Volume Solids | 76±2% |
| VOC | 256g/L,accord with EU Dircrtive2004/42/EC,subcategory j |
| Volatile organic compound content | 256 g/L, complying with EU Solvent Emissions Directive 2004/42/EC, subcategory j |
| Flash Point | Greater than 20°C |
| Flash Point | Above 20 °C |
| Film thickness | Dry : 75-200 µm/coat Wet : 98-263µm/coat |
| Applied film thickness | DFT: 75–200 µm per coat; WFT: 98–263 µm per coat |
| Theoretical Coverage | 6.08m2/Ltr/125 microns |
| Theoretical spreading rate | 6.08 m²/L / 125 µm |
Practical coverage depending on surface conditions, environment, applications, etc.
| Application Temperature | 5°C-40°C |
|---|---|
| Mixing | Combine Base with Hardener, mix thoroughly with power agitator |
| Mixing | Mix the base and curing agent and stir thoroughly with a power tool |
| Mixing Ratio | Base/Hardener=9/1(by weight) |
| Mixing ratio | Base : curing agent = 9:1 (by mass) |
| Pot life | 5°C | 10°C | 20°C | 30°C |
| Pot life | 8hrs | 6hrs | 3hrs | |
| Application Methods | Airless spray, air spray, brush and roller |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.