Inorganic Zinc Silicate Anti-corrosive E06-1

Browse Similar Models by CategoryThis model belongs to: Primer, Inorganic Zinc Silicate

Composition

Two-component, composed of alkyl silicate polymer, zinc dust, pigments, additives and alcohol solvents

Inorganic zinc silicate anti-corrosive paint.

Key characteristics

• The zinc dust provides cathodic protection, with high anticorrosive performance
• Fast-drying; can be handled and stacked after a short time.

High heat resistance; the film withstands temperatures up to 400°C.

• Good low-temperature curing properties
• Excellent solvent resistance

High impact resistance, good abrasion resistance and moderate flexibility.

• Compatible with most coating systems
• Type-approved by China Classification Society

Application parameters

Minimum recoating interval: more than 24 h; before painting, wipe the surface of the E06-1 film with a cloth dipped in Thinner 107,

to determine whether the film is fully cured. If zinc dust dissolves on the cloth, the film is not fully cured,

and it must continue drying; when relative humidity is below 70%, water may be sprinkled on the film to promote film

curing; dry until the cloth is colourless (no dissolution), indicating that the film is fully cured, before proceeding

to apply the next coat. The maximum recoating interval is unlimited, but zinc salts must be removed before recoating.

Subsequent coat

Can be used in combination with chlorinated rubber, epoxy, epoxy bitumen, bituminous, polyurethane, vinyl and other coatings

but cannot be used in combination with oil-based, alkyd or polyester paints.

Substrate Temperature

• May be applied at air temperatures from -20 °C to 50 °C

When the substrate temperature is too high (≥ 40 °C), spray application is required, but the substrate temperature shall not

exceed 60 °C. To avoid dry spray, add Thinner 107 until dry spray is eliminated

• Substrate temperature must be at least 3 °C above the dew point

Application method

Precautions

Stir continuously with a mixer during application to prevent zinc dust from settling.

During application at temperatures above 30°C, to prevent dry spray, Thinner 107 may be added

until dry spray no longer occurs; the amount of Thinner 107 added is 0–10% of the paint weight.

When the dry film thickness is below the requirement and one additional coat of E06-1 inorganic zinc silicate anti-corrosive paint is required,

E06-1 inorganic zinc silicate anti-corrosive paint should be diluted with 50% Thinner 107 before recoating to improve intercoat adhesion between films.

The film thickness of E06-1 inorganic zinc silicate anti-corrosive paint must not exceed 120 µm; if the dry film thickness is greater

than 120 µm, mud cracking and failure will occur due to internal stress in the film.

To seal the pores on the surface of the inorganic zinc silicate anti-corrosive paint film and prevent pinhole corrosion, use

H53-42 epoxy sealer or other sealer to seal E06-1 inorganic zinc silicate anti-corrosive paint.

Before applying the next coat of paint, the film of E06-1 inorganic zinc silicate anti-corrosive paint must be fully cured,

otherwise intercoat adhesion and anti-corrosion performance will be affected. Before painting, use a cloth dipped in Thinner 107

to wipe the film; if no colour appears on the cloth (that is, no dissolution), the film is fully cured, and the subsequent coat may then be applied.

Relative humidity below 70% is unfavourable to the hydrolytic curing reaction of inorganic zinc silicate anti-corrosive paint; to promote

film curing, sprinkle water appropriately on the film every 2 h starting 3 h after application.

The maximum recoating interval for E06-1 inorganic zinc silicate anti-corrosive paint is unlimited, but before applying the next

coat of paint, zinc salts formed on the film surface must be thoroughly removed; otherwise the intercoat adhesion and protective effect of the film will be affected.

Disclaimer

The above information and data for this product are accumulated from our tests and practical experience

accumulated, and may serve as an application guide. For application carried out under conditions unknown to us, we

We guarantee only the quality of the paint itself and accept no responsibility for other matters. We

and reserve the right to make modifications as the product is improved.

Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.