Silver Silicone High-temperature Baking Paint 14 is a heat-resistant paint, a silicone coating system. Suitable for steel surfaces of high-temperature equipment such as boilers, engine housings, exhaust pipes, chimneys and ovens. A high-temperature paint composed of silicone resin, aluminium powder and organic solvents etc. Has good heat resistance, and can be used in the range of 300 °C–500 °C. Parameters on this page: volume solids 39 ± 3%, dry film thickness 20 µm, theoretical spreading rate 55 g/m².
Data source: KAILIN original Technical Data Sheet (TDS), "Silver Silicone High-temperature Baking Paint 14"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 39 ± 3% |
|---|---|
| Dry Film Thickness | 20µm |
| Theoretical Spreading Rate | 55 g/m² |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | — |
| Flash Point | 7 °C; drying time (200 ± 2 °C) ≤3 h |
| Thinner | Xylene |
| Colour / Appearance | Silver, smooth film |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
| Composition | A high-temperature paint composed of silicone resin, aluminium powder and organic solvents etc. |
|---|
Good heat resistance, usable in the range 300–500 °C
| Use | Suitable for steel surfaces of high-temperature equipment such as boilers, engine housings, exhaust pipes, chimneys and ovens. |
|---|---|
| Appearance | Silver, smooth film |
| Volume Solids | 39 ± 3% (measured according to GB/T 9272 eqv ISO 3233:1998) |
|---|---|
| Dry Film Thickness | 20µm |
| Wet Film Thickness | 51µm |
| Theoretical quantity | 55g/m² |
| Flash | Flash point 27 °C; drying time (200 ± 2 °C) ≤3 h |
| Recoat interval | After the first coat is baked dry, wait until it cools before applying the second coat. |
| Recommended number of coats | 1–2 coats, dry film thickness 20–40 µm. |
May be applied directly over steel prepared to Sa 2.5
E06-1 Inorganic Zinc Silicate Anticorrosive may also be used as the primer to improve anticorrosive performance. Generally
E06-1 inorganic zinc silicate anti-rust paint one coat (40 µm), Silver Silicone High-temperature Baking Paint 14 1–2 coats (20–40 µm) is recommended
Mill-scale-free steel: grind with abrasive discs to St 3
Steel with existing coating: abrasive blast clean to Sa 2.5; or remove all old coating and grind with abrasive discs to St 3
For best results, after applying the first high-temperature coat, heat to the service temperature, and apply the second coat after cooling
The substrate temperature must be at least 3 °C above the dew point, but not more than 60 °C
| Airless Spray | |
| Thinner | Xylene |
| Thinning quantity | 0–5% (by paint weight, but normally no thinning required) |
| Nozzle tip size | 0.4-0.5mm |
| Spray output pressure | 12–15 MPa (approx. 120–150 kg/cm²) |
| Air Spray | |
| Thinner | Xylene |
| Thinning quantity | 0–5% (by paint weight, but normally no thinning required) |
| Nozzle tip size | 2.0-3.0mm |
| Air pressure | 0.3–0.5 MPa (approx. 3–5 kg/cm²) |
| Roller/brush | Thinning generally not required |
|---|---|
| Cleaning solvent | Xylene |
| Safety measures | See the Safety Data Sheet (MSDS) of Shanghai Kailin Paint Factory. |
| Packaging | 4 L drum, 4 kg |
| Shelf Life | 6 months. |
| Notes | To use this product correctly, read the Application Guide in this data sheet carefully. |
The above information and data for this product are accumulated from our tests and practical experience
accumulated, and may serve as an application guide. For application carried out under conditions unknown to us, we
We guarantee only the quality of the paint itself and accept no responsibility for other matters. We
and reserve the right to make modifications as the product is improved.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.